Abstract:In this study, the recycled Al-Mg-Mn-Fe alloys having different Fe levels (0.1%, 0.5%, and 0.8%) were successfully developed by applying squeeze casting without heat treatment. Optical and scanning electron microscopy, synchrotron X-ray tomography and radiography, X-ray diffraction, and tensile tests combined with thermodynamic calculations were used to study the correlation between the microstructural evolution and mechanical properties. The results showed that for the alloys with an applied pressure of 75 MPa, as the Fe increase from 0.1% to 0.8%, the yield strength (YS), and ultimate tensile strength (UTS) increased from 122 MPa and 244–146 MPa and 289 MPa, and elongation decreased from 34% to 12%. Even though Fe additions increased the volume fraction of Fe-rich intermetallic phases, it significantly increased the UTS and YS. The synchrotron X-ray tomography and deep-etched results both show that the 3D morphology changed from individual Chinese-script to interconnected plate-like. The 3D morphology of 0.8Fe alloy clearly demonstrate that the hole partially or whole penetrated the entire rectangle-shaped Al6(FeMn) phases, which is due to the close-packed plane growth. In-situ synchrotron X-ray radiography results showed the facet growth behaviour of Al6(FeMn) in 0.8Fe alloys during solidification with a long needle-like shape. The size of primary Al6(FeMn) phases decreases, whereas their number increases with increasing cooling rate. Moreover, the applied pressure was beneficial in refining the size of α-Al grains and Fe-rich phases and reducing the volume fraction of pores, thus contributing to the improvement of strength and elongation. The in-situ tensile test results indicated that the crack initiated in the Fe-rich phases and pores, and the slip lines were blocked by the Fe-rich phases resulting in the strengthening of the secondary phases.

Synchrotron X-ray tomography investigation of 3D morphologies of intermetallic phases and pores and their effect on the mechanical properties of cast Al-Cu alloys

Synchrotron X-ray tomography investigation of 3D morphology of intermetallic phases and pores and their effect on the mechanical properties of cast Al-Cu alloys

3D Characterisation of the Fe-rich intermetallic phases in Al-5%Cu alloys by synchrotron X-ray microtomography and skeletonisation

Revealing the influence of Fe on Fe-rich phases formation and mechanical properties of cast Al-Mg-Mn-Fe alloys

Effect of ultrasonic melt processing and cooling rate on microstructure evolution of Al–Cu–Mn–Mg–Fe–Si alloy

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Study of the evolution mechanisms of Fe-rich phases in Al-Si-Fe alloys with Mn modification using synchrotron X-ray imaging

Effect of Ti on Microstructure and Mechanical Properties of Die-Cast Al-Mg-Zn-Si Alloy

Exploring crystal structures, stability and mechanical properties of Fe, Mn-containing intermetallics in Al-Si Alloy by experiments and first-principles calculations

3D characterization of ultrasonic melt processing on the microstructural refinement of Al-Cu alloys by synchrotron X-ray tomography

The characterization of Fe-rich phases in a high-pressure die cast hypoeutectic aluminum-silicon alloy

Effect of Si on Fe-rich intermetallic formation and mechanical properties of heattreated Al-Cu-Mn-Fe alloys

Effect of Fe and Mn Content on the Microstructures and Tensile Behaviour of AlSi7Cu3 Alloy: Thermal Analysis and Tensile Tests

Microstructure evolution and nano-phases strengthening of Al-5%Cu alloy by adding trace AlSiTiCrNiCu high entropy alloy

Multi-scale iron-rich phases induce fine microstructures in Al-Zn-Mg-Cu-Fe alloys

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Morphology, thermal stability, electronic structure and mechanical properties of α-AlFeMnSi phases with varying Mn/Fe atomic ratios: Experimental studies and DFT calculations

The composite microstructures’ effect on the mechanical properties of Ni–25Al–xFe intermetallics

Microstructural evolution and mechanical properties of cast Al‐2.6Li‐2.8Mg‐(0.5, 1.4)Cu‐0.2Zr‐0.2Sc alloys during heat treatment

Effect of Fe-Rich Phases on Fracture Toughness of High Strength Al-Zn-Mg-Cu Alloy

Evolution of the Second-Phase Particles and Their Effect on Tensile Fracture Behavior of 2219 Al-xCu Alloys