Abstract:In this work, we report the evolution behavior of Fe and Fe-rich phases in the high-Fe concentration recycled Al-Si-Mg aluminum melt with and without alloying elements (Mn, Cr, Co) introduced. Firstly, the thermodynamic calculations reveal that the addition of Mn, Cr, and Co could improve the nucleation temperature of the Fe-rich phase. Moreover, four solidified ingots for Al-10Si-0.5Mg-1Fe alloy(base alloy) and the base alloy with 1.3 wt% Mn, 0.8 wt% Cr, and 0.8 wt% Co added, respectively, were prepared by holding the melt for 30 min at 610 °C after all the raw materials were fully melted. Microstructure examination revealed that the addition of Co resulted in the formation of the needle-like Fe-rich phase, which further leads to a poor settling effect and low iron removal efficiency. In contrast, the addition of Mn and Cr favors converting β-AlFeSi into α-AlFeMnSi, and forming the Chinese script and fish-bone Fe-rich phase. The size of the Fe-rich phase formed after adding Cr is smaller, while the residual Fe content after adding Mn is less. Also, the sludge phase at the bottom of the ingot presents a polygonal shape and long rod shape after adding Mn and Cr, respectively. Further, the Mn alloying increases the particle size of the sludge, while Cr refines the sludge phase and increases the aspect ratio (length/width ratio) of the sludge. Particularly, for Al-Si-Mg alloy with 1.0% Fe content, the superior mechanical properties are obtained by adding 0.8 wt% Cr, and the tensile strength reaches 136 MPa. After adding 1.3 wt% Mn, the Fe content of the upper section is reduced to 0.37 wt%, and the Fe removal rate achieves 63%. The obtained results provide some guidelines for achieving high iron separation efficiency in recycled aluminum-silicon alloy melts.

Effect of Cooling Rate and Co Content on the Formation of Fe-rich Intermetallics in Hypoeutectic Al7Si0.3Mg Alloy with 0.5%Fe

Effect of Co Addition on the Phase Structure and Magnetic Properties of Fe-Si-Al Alloys

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy

Evolution behavior of Fe and Fe-rich phases in high-Fe concentration Al-Si-Mg alloy with Mn, Cr, and Co alloyed

Uncovering the effects of neutralizing elements (Co, Mn and Cr) on the Fe-rich intermetallic formation in Al–Si–Cu alloys

Effect of Si on Fe-rich intermetallic formation and mechanical properties of heattreated Al-Cu-Mn-Fe alloys

Crystallization behavior, soft magnetic properties and good bending ductility of high Fe content FeSiBCuPC alloys induced by composition design

The Effect of Fe Content on the Solidification Pathway, Microstructure and Thermal Conductivity of Hypoeutectic Al–Si Alloys

Microstructure evolution and metastable phase formation in undercooled Fe–30 at.% Co melt

Study of the evolution mechanisms of Fe-rich phases in Al-Si-Fe alloys with Mn modification using synchrotron X-ray imaging

Effect of ultrasonic melt processing and cooling rate on microstructure evolution of Al–Cu–Mn–Mg–Fe–Si alloy

Effect of Fe and Mn Content on the Microstructures and Tensile Behaviour of AlSi7Cu3 Alloy: Thermal Analysis and Tensile Tests

The Influence of the Silicon Content on the Formation of Fe23B6 Metastable Phases in Fe65Co11−xB20SixZr2Hf2 Bulk Amorphous Alloys

Unusual alloying effects of Co and Ni on structure and magnetic properties of Fe-Si-B-Cu nanocrystalline alloys with pre-existing α-Fe nanocrystals

Evolution of Constitution, Structure, and Morphology in FeCo-Based Multicomponent Alloys

The influence of Co on the magnetic properties of Fe-Si-B-Nb-Cu system

Solidification microstructure manipulation mechanism of hypoeutectic and hypereutectic Al-Si alloys controlled by trace in-situ nano-Fe 2 B and nano-Fe 3 Si

Effect of Si/Al addition on magnetic properties of Fe-Co alloy

The influence of cooling rate and manganese content on the β-Al5FeSi phase formation and mechanical properties of Al–Si-based alloys

Effect of Cooling Rate on the Microstructure Evolution and Mechanical Properties of Iron-Rich Al–Si Alloy

Exploring crystal structures, stability and mechanical properties of Fe, Mn-containing intermetallics in Al-Si Alloy by experiments and first-principles calculations