Abstract:Canada’s long-term plan for used nuclear fuel includes permanent disposal in a deep geological repository (DGR) using a multiple-barrier system with a key barrier being the used fuel container (UFC). The UFC design consists of an inner vessel of carbon steel (CS), which provides the structural strength to withstand repository loads, and an outer layer of copper, which functions as an external corrosion barrier. The inner vessel of the current UFC design is composed of a pressure grade CS hemispherical head and pressure grade CS piping as a body, the two parts to be laser welded on-site. One of potential issues with this design is the effect of g-radiation on corrosion of the crevice near the weld region. The environment inside the sealed UFC would be humid air. Gamma-irradiation of humid air produces NOx and HNO3, and these species could accelerate the formation and condensation of water droplets in crevices (which might also have surface roughness features that act as preferential condensation sites). The chemical environment in such acidic condensed water, coupled with the presence of oxidizing water radiolysis products, could be very aggressive. Corrosion within the crevice between the head and the body of the container assembly or in the stressed regions near the welds could lead to a localized build-up of corrosion products (oxide deposits and H2gas). The effect of g-radiolysis on crevice corrosion of CS is being investigated using a combination of corrosion exposure tests and electrochemical measurements. These measurements are augmented by post-test analysis of oxide surface using SEM, XPS and Raman spectroscopy. In the corrosion tests reported here, a prepared CS crevice was wetted by adding a couple of water droplets to the mouth of the crevice. The test sample was then exposed to a desired environment in a sealed container for 20 h. Optical images of the corroded surfaces show that the corrosion of the wet bold surface progresses more extensively in air than in Ar, more at 80 oC than at 25 oC and more in the presence rather than in the absence of radiation. The composition of the oxide formed on the wet bold surface (as determined by Raman spectroscopy) shows the oxidation leads to formation of a mixed FeII/FeIII oxide/hydroxide in Ar, and to the formation of FeIII oxyhydroxide and FeIII oxide in addition to the FeII/FeIII oxide in air. Increasing temperature increases the ratio of oxide to hydroxide or oxyhydroxide but does not affect the metal oxidation states. More corrosion products are formed in the presence than absence of radiation. In contrast to the bold surface the interior surface of crevice remained smooth. The XPS analysis of the crevice surface indicates that the oxides formed there are thin (< ~ 9 nm) and that a larger fraction of the oxide is FeIII oxide/hydroxide rather than FeII/FeIII oxide. The thickness of the oxide formed at 80 oC is slightly higher than that formed at 25 oC. Radiation slightly decreases the oxide thickness at 25 oC while it increases the oxide thickness at 80 oC. The different corrosion behaviours of the crevice and bold surfaces raise the possibility of galvanic coupling between the two surfaces. This galvanic effect was investigated by monitoring the coupling current between two electrodes, one electrode representing the bold surface and the other representing the crevice surface, in the electrochemical coupling tests. To aid in interpretation of the galvanic coupling experiments, the corrosion potential and linear polarization measurements were made on each electrode separately. The post-test surfaces from these tests were examined by SEM and XPS. The observed effects of temperature and g-radiation on the corrosion potentials are consistent with the different oxide formation and growth observed in the coupon exposure study. The corrosion potential on the crevice electrode is always slightly higher than that of a bold electrode with the difference depending on temperature and radiation environment. A galvanic coupling current observed between the two electrodes shows that the crevice electrode is the net cathode. The measured coupling currents are consistent with the results from the dynamic polarization tests performed on each electrode. A CS crevice corrosion mechanism that can explain both the crevice corrosion tests and the electrochemical results is discussed.

Effect of Cumulative Gamma Irradiation on Microstructure and Corrosion Behaviour of X65 Low Carbon Steel

Characterization of Corrosion Behavior of Irradiated X65 Low Carbon Steel in Aerobic and Unsaturated Gaomiaozi Bentonite

Effect of Irradiation Grafting Epoxy on Surface Characteristics of Carbon Fibers and Mechanical Properties of Composites

Studies on Corrosion Behaviour of Low Carbon Steel Canister with and Without Γ-Irradiation in China’s HLW Disposal Repository

Irradiation Effects of Carbon Fibers in C/SiC Composites

Corrosion Behaivour of X65 Low Carbon Steel During Anaerobic Period of High Level Nuclear Waste Disposal

Influence of irradiation number of high current pulsed electron beam on the structure and properties of M50 steel

The Effect on Carbon Fiber Surface Structure and Tensile Strength Irradiated by Γ-Ray

Effect of Gamma Irradiation on Microstructural Evolution and Mechanical Properties of Sn3ag0.5cu Solder Joints

The Effect of Gamma Ray Irradiation on Pan-Based Intermediate Modulus Carbon Fibers

Localized Corrosion of Carbon Steel in the Presence of Gamma Radiation

Crevice Corrosion of Low Alloy Steel and Carbon Steel in the Simulated Groundwater at 90 Degrees C

Corrosion Behavior and Mechanism of Irradiated 304 Nuclear Grade Stainless Steel in High-Temperature Water

Effect of Γ Irradiation on the Properties of Basalt Fiber Reinforced Epoxy Resin Matrix Composite

Experimental Study on Effects of Residual Sewage Sludge by Gamma-ray Irradiation Treatment

Investigation of Relationship Between Cooling Rate, Microstructure, Porosity and Corrosion in As-Cast Samples of the 1050 Aluminum Alloy Subjected to Different Levels of Gamma Radiation

Effect of Hydrogen Uptake on the Electrochemical Corrosion of N18 Zircaloy under Gamma Irradiation

Effect Of Cr Content On The Electrochemical Behavior Of Low-Chromium X65 Steel In Co2 Environment

Effect of gamma irradiation on microstructural evolution and mechanical properties of SnPb eutectic solder joints

Effect of Co60gamma Ray Irradiation for Carbon Fibre on Interfacial Properties in Epoxy Resin Composites

Clarifying the mitigation effect of proton irradiation on the intergranular oxidation of 316L stainless steel in high temperature water