Abstract:The widespread use of sodium aluminosilicate glass in many engineering applications due to its mechanical and optical properties (transparency, dielectric, etc.), has become common in recent years. However, glass, a brittle material, has its vulnerability to fracture. Processes such as heat treatment (heat tempering) or chemical strengthening through ion-exchange have been used to create residual stress profiles on the glass, in a bid to improve its fracture strength. However, failure still occurs, which is mostly catastrophic and expensive to repair. Therefore understanding, predicting, and eventually improving the resistance to damage or fracture of chemically strengthened glass is important to designing new glasses that would be tougher while retaining their transparency. The relationship between the glass residual stress parameters such as the compressive stress (CS), depth of compression layer (DOL), and central tension (CT) versus apparent (effective) fracture toughness for different crack depth was investigated in this study using a Silicon Carbide particle blast plus ring-on-ring (RoR) test method. The results also showed that improving the fracture resistance of glass via chemical strengthening requires a proper combination of CS, DOL, and CT, which is particularly dependent on the initial/existing crack (flaw) depth. It was determined that for a damage event involving the introduction of a shallow crack depth, the criterion for optimal resistance to fracture, in terms of apparent fracture toughness, is weighted more towards a high CS, than deep DOL while for a deep flaw damage event, it is more weighted towards deep DOL, than a high CS. These results provide a valuable piece of information in the design of a more robust glass in engineering applications.

Dynamic Crack-Interface Interactions in SGP Laminated Glass: an Experimental Investigation

Soft Impact Response of Laminated Glass Plates

Deformation and Damage Mechanisms of Laminated Glass Windows Subjected to High Velocity Soft Impact

Investigation of Dynamic Multi-Cracking Behavior in PVB Laminated Glass Plates

Investigation on Behavior of Glazing System with Elastomeric Interlayers under Blast Effects

Investigation on Dynamic Propagation Characteristics of In-Plane Cracks in PVB Laminated Glass Plates

Different Driving Mechanisms of In-Plane Cracking on Two Brittle Layers of Laminated Glass

Development of a dynamic model for crack propagation in glazing system under thermal loading

Modeling And Experimental Studies Of Crack Propagation In Laminated Glass Sheets

Experimental Study of Dynamic Fracture Behavior of PVB Laminated Glass by High-Speed Photography

Scratch-induced micro-fracture behaviour and translational failure of glass: An experimental and numerical study

Experimental and analytical study on the pre-crack impact response of thick multi-layered laminated glass under hard body impact

Experimental investigation on the radial and circular crack propagation of PVB laminated glass subject to dynamic out-of-plane loading

An Analytical Model for Deformation and Damage of Rectangular Laminated Glass under Low-Velocity Impact

Experimental and macroscopic investigation of dynamic crack patterns in PVB laminated glass sheets subject to light-weight impact

033 Crack initiation and path prediction of float glass with various constrain conditions under thermal loading

An Ordinary State-Based Peridynamic Modeling for Dynamic Fracture of Laminated Glass under Low-Velocity Impact

Fracture Behavior of A Four-Point Fixed Glass Curtain Wall under Fire Conditions

Experiment and Numerical Simulation of Damage Progression in Transparent Sandwich Structure under Impact Load

Dynamic Structural Response of Laminated Glass Panels to Blast Loading

The Competing Effect of Initial Crack Depth Versus Chemical Strengthening Parameters on Apparent Fracture Toughness of Sodium Aluminosilicate Glass