Abstract:<p>This study presents a combined experimental and analytical study on the impact response of multi-layered laminated glass (MLG) under low-velocity hard body impact before glass breakage. The drop weight impact tests using repeated attempts with increasing impact velocities were firstly performed on 12 MLG panels with double PVB or SG interlayers to record the impact response, high speed fracture process. The experimental results identify that: (1) the indentation is the predominant factor for glass fracture in the examined impact scenarios; (2) the key time interval of the pre-crack impact response is within 0.6 ms. The indentation which hasn't been considered in the existing analytical works was hence introduced into the proposed nonlinear analytical model, which employed third order shear deformation theory and obtained the solutions of motion equations by a two-step perturbation method, according to the former finding. The calculated impact response based on the proposed model was validated with the experimental results within 0.6 ms based on the latter finding and showed satisfactory agreement.</p><p>A parametric study was subsequently conducted to investigate the influence of factors such as the number of glass layers, glass thickness and ratio, panel size on the pre-crack impact response. The results show the increase of peak force and indentation is more sensitive to the increase of total glass thickness after the thickness reaches 24 mm and presents less sensitivity when the thickness approaches 57 mm. The variation of the glass thickness ratio has no influence on the pre-crack behavior once the total glass thickness is fixed.</p>

Experimental and macroscopic investigation of dynamic crack patterns in PVB laminated glass sheets subject to light-weight impact

Experimental investigation on the radial and circular crack propagation of PVB laminated glass subject to dynamic out-of-plane loading

Experimental Study of Dynamic Fracture Behavior of PVB Laminated Glass by High-Speed Photography

Investigation of Dynamic Multi-Cracking Behavior in PVB Laminated Glass Plates

Investigation on Dynamic Propagation Characteristics of In-Plane Cracks in PVB Laminated Glass Plates

Modeling And Experimental Studies Of Crack Propagation In Laminated Glass Sheets

Experimental study on mechanical behavior of PVB laminated glass under quasi-static and dynamic loadings

Soft Impact Response of Laminated Glass Plates

Deformation and Damage Mechanisms of Laminated Glass Windows Subjected to High Velocity Soft Impact

Quantity Effect Of Radial Cracks On The Cracking Propagation Behavior And The Crack Morphology

Post-fracture performance of laminated glass panels under consecutive hard body impacts

Experimental study on the gradual fracture of layers in multi-layer laminated glass plates under low-velocity impact

Experimental and analytical study on the pre-crack impact response of thick multi-layered laminated glass under hard body impact

Experimental Investigation on the Impact Resistance of Laminated Glass with Various Glass Makeups

Different Driving Mechanisms of In-Plane Cracking on Two Brittle Layers of Laminated Glass

Numerical Study of Pvb Laminated Windshield Cracking Upon Human Head Impact

Influences of temperature and impacting velocity on dynamic failure of laminated glass: Insights from peridynamic simulations

Dynamic Crack-Interface Interactions in SGP Laminated Glass: an Experimental Investigation

An Ordinary State-Based Peridynamic Modeling for Dynamic Fracture of Laminated Glass under Low-Velocity Impact

Research on Dynamic Response of PVB Laminated Windshield Subjected to Low Velocity Impact

Experimental investigation on constitutive behavior of PVB under impact loading