Abstract:The integration of low-alloy steel reinforcement (LS) with seawater sea-sand concrete (SSC) offers an opportunity for marine infrastructure construction that utilizes local resources, such as seawater and sea-sand, while ensuring exceptional durability of structures in challenging environments. However, the cracking of the concrete cover resulting from rebar corrosion remains the primary factor contributing to the deterioration of reinforced-concrete structures exposed to marine environments. In this study, an external current was applied to accelerate the corrosion process of both LS and ordinary steel bars (OS), which were embedded in SSC that was shallowly buried in a wet-salt sand environment. To accurately determine the timing and location of SSC cover cracking, Digital Image Correlation (DIC) technology was utilized. Microscopic analysis was conducted to examine the morphology, phase composition, and content of each component of the corrosion products. Then, the expansion coefficients of the corrosion products of the rebars embedded in SSC with different water–binder ratios were determined. The results indicated that the primary corrosion products formed on OS are α-FeOOH, β-FeOOH, γ-FeOOH, Fe 2 O 3 , and Fe 3 O 4 , which form a porous structure. In comparison, corrosion products of LS are fundamentally similar to those of OS but include Cr 2 O 3 , producing a compact rust layer for better steel protection. Furthermore, the corrosion products of LS exhibit a lower expansion coefficient compared to those of OS in SSC with an identical water–binder ratio. Finally, the cracking time of the SSC cover, as determined through DIC, was validated through the use of a conventional prediction model.

Corrosion products and corrosion-induced cracks of low-alloy steel and low-carbon steel in concrete

Study On Distribution Of Steel Corrosion Products In Concrete Structures

On the Penetration of Corrosion Products from Reinforcing Steel into Concrete Due to Chloride-Induced Corrosion

Distribution of millscale on corroded steel bars and penetration of steel corrosion products in concrete

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Experimental Study on Distribution of Corrosion Products in Corrosion-Induced Cracks in Reinforced Structures

Mill Scale and Corrosion Layer at Concrete Surface Cracking

Corrosion resistance of low-alloy steel in concrete subjected to long-term chloride attack: Characterization of surface conditions and rust layers

Corrosion Damages of Reinforced Concrete Characterized by X-ray CT and DVC Techniques

Influence of Environment on the Development of Corrosion Product-Filled Paste and a Corrosion Layer at the Steel/concrete Interface

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams

Corrosion Development of Carbon Steel Grids and Shear Connectors in Cracked Composite Beams Exposed to Wet-Dry Cycles in Chloride Environment.

Modelling the corrosion mechanism of steel bars in chloride-contaminated concrete with transverse cracks

Analysis on steel corrosion at the cracking of concrete

Crack shape and rust distribution in corrosion-induced cracking concrete coupled with load

Microscopic Analysis of Steel Corrosion Products in Seawater and Sea-Sand Concrete

Corrosion products of low-alloy steel bars and their induction of cracking in seawater sea-sand concrete cover

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

Investigation of corrosion-induced cracks using corrosion products quantified by an X-ray technique and FE analysis of single- and multiple-rebar beams

Shear Performance of Reinforced Concrete Beams with Corroded Stirrups in Chloride Environment

Fractal Characteristics of Corrosion-Induced Cracks in Reinforced Concrete.