Abstract:This study conducted a deep investigation of TiO 2 nanotube (TNT) layers of two different thicknesses anodically grown on electrodeposited Ti films. The Ti films were grown from molten salts on Ni foils. The structure of the starting metals was compared by XRD (X-Ray Diffraction) and EBSD (Electron Backscatter Diffraction analyses), which showed a strong orientation towards the titanium (101) for the electrodeposited substrate, compared to rather polycrystalline structure of the rolled Ti. The photoelectrochemical and electrochemical properties of 1 μm and 5 μm thick TNT layers anodically grown on these substrates were examined and compared with TNT layers of the same thickness. No significant morphological and compositional differences were found using SEM (Scanning Electron Microscopy) and XPS (X-ray Photoelectron Spectroscopy) between the TNT layers grown on the two substrates. However, higher photocurrent densities and ICPE values were observed for TNT layers grown on electrodeposited Ti. An in-depth investigation using Cyclic Voltammetry (CV) and Electrochemical Impedance Spectroscopy (EIS) analyses showed increased conductivity of the TNT layers produced on electrodeposited Ti compared to their counterparts. The carrier density ( N D ) for the TNT layers on electrodeposited Ti, calculated from Mott-Schottky measurements, showed a higher doping level than the TNT layers grown on Ti foils. This increase in N D results in more optimal photoelectrochemical performance of the TNT layers grown on electrodeposited Ti. All in all, the results presented herein pave the way for the use of electrodeposited Ti, with all its inherent benefits, and allow the further study of its promising properties in a wide range of applications.

Influence of Prior Passivation on Characteristics of TiO2Nanotube Arrays Fabricated on Ti Foil in a HF+H2SO4Solution

Characteristics and Electronic Properties of Self-Organized Tio2 Nanotube Arrays Fabricated on Ti Foil by Square Wave Pulse Anodizing Ti in an Hf + H2so4 Solution

Effect of Acid Solution, Fluoride Ions, Anodic Potential and Time on the Microstructure and Electronic Properties of Self-Ordered TiO 2 Nanotube Arrays

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

The Effect of Initial Etching Sites on the Morphology of TiO2 Nanotubes on Ti-6Al-4V Alloy

Controlling anodization time to monitor film thickness, phase composition and crystal orientation during anodic growth of TiO2 nanotubes

Influence of Square Wave Anodization on the Electronic Properties and Structures of the Passive Films on Ti in Sulfuric Acid Solution

Fabrication and Formation Mechanism of Triple-Layered Tio2 Nanotubes

Can electrodeposited Ti replace rolled Ti as substrate for the growth of anodic TiO 2 nanotube layers?

Fabrication of Titanium Oxide Nanotube Arrays by Anodic Oxidation

Phosphoric anion layer inhibits electronic current generation and nanotube growth during anodization of titanium

Fabrication and Field Emission Characteristics of TiO2 Nano-Tube Arrays

Preparation of TiO2 Nanotube Photocatalyst by Anodization and Improvement of Photocatalytic Performance

Effect of anodization conditions on the synthesis of TiO2 nanopores

Electrochemical behavior and effect of heat treatment on morphology, crystalline structure of self-organized TiO2 nanotube arrays on Ti-6Al-7Nb for biomedical applications

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

Causes for the Formation of Titania Nanotubes During Anodization

Anodic TiO2 Nanotubes for Hydrophobic Coatings and Photo-electrochemical Water Splitting Application

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays

Fabrication of open-ended TiO2 nanotube arrays by anodizing a thermally evaporated Ti/Au bilayer film

Facile fabrication of open-ended high aspect-ratio anodic TiO 2 nanotube films and their applications