Abstract:Mg–Zn–Y–Nd alloy was prepared by casting and hot extrusion. The microstructure and mechanical properties of OM, SEM, XRD, TEM, and tensile tests were investigated with casting and hot extruded alloys. The results demonstrate that in a casting Mg–Y–Nd–Zr alloy, the α-Mg matrix is separated into the cell structure by a discontinuously distributed coarse Mg24Y5/α-Mg eutectic structure and fine Mg12Nd particles. TEM analysis shows that the Mg12Nd and Mg24Y5 phases have the orientation of \( {\left[001\right]}_{{\mathrm{Mg}}_{12}\mathrm{Nd}}//{\left[0221\right]}_{\upalpha -\mathrm{Mg}} \), and \( {\left[111\right]}_{{\mathrm{Mg}}_{24}{\mathrm{Y}}_5}//{\left[0001\right]}_{\upalpha -\mathrm{Mg}} \) and \( {\left(10\overline{1}\right)}_{{\mathrm{Mg}}_{24}{\mathrm{Y}}_5}//{\left(10\overline{1}0\right)}_{\upalpha -\mathrm{Mg}} \), respectively. The hot extrusion separates the Mg24Y5/α-Mg eutectic structure into fragments and aligns fragmentary Mg24Y5 particles along the extrusion direction. The interaction of hot extrusion and strengthening particles refines the α-Mg matrix greatly. Moreover, large strains result in the stacking faults of the matrix. As compared to the casting alloy, the hot-extruded one exhibits high yield strength, ultimate tensile strength, and elongation, which should be ascribed to the grain fineness, optimum distribution of strengthening particles and multiple substructures.

Microstructure and Mechanical Properties of Mg-Nd-Zn-Zr Billet Prepared by Direct Chill Casting

The Effect of Casting Speed on Microstructure, Microsegregation, and Mechanical Properties of High-Strength Mg-Nd-Zn-Zr Alloy

Effect of Process Parameters on Structure and Macrosegregation Upon Direct Chill Casting of Mg–Nd–Zn–Zr Alloy

Microstructures and Macrosegregation of Al–Zn–Mg–Cu Alloy Billet Prepared by Uniform Direct Chill Casting

Mechanical properties and microstructure of a high-quality Mg-Nd alloy ingot with large size manufactured by direct chill casting

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Effect of Direct Chill Casting Process Parameters on the Microstructure and Macrosegregation of Mg-Al-Zn Ingot

Microstructures and Mechanical Properties of 584 mm 7055 Alloy Billet by Direct Chill Casting Under Annular Electromagnetic Stirring Coupled with Intercooling

Microstructures and Mechanical Properties of As-Cast and As-Extruded Mg-4.50zn-1.13ca (wt%) Alloys

The Microstructure and Mechanical Properties of As-cast Mg-10Gd-3Y-xZn-0.6Zr (x=0, 0.5, 1 and 2 Wt%) Alloys

Microstructure and Mechanical Properties of As-Cast and Extruded Mg–8Li–3Al–2Zn–0.5Nd Alloy

Forgeability and Die-Forging Forming of Direct Chill Casting Mg–Nd–Zn–Zr Magnesium Alloy

Microstructure and Mechanical Properties of Extruded Mg-Zn-Nd-Y-Zr-Ca Alloy

Microstructure and mechanical properties of the Mg-Gd-Y-Zn-Zr alloy fabricated by semi-continuous casting

Microstructure and mechanical properties of NZ30K alloy by semi-continuous direct chill and sand mould casting processes

Microstructure and mechanical properties of Mg–4Al–4Nd–0.5Zn–0.3Mn alloy

Microstructure and Mechanical Properties of WE43 Magnesium Alloy Fabricated by Direct-Chill Casting

Hot Extrusion Effect on the Microstructure and Mechanical Properties of a Mg–Y–Nd–Zr Alloy

Microstructure evolution and mechanical properties of an ultra-high strength casting Mg–15.6Gd–1.8Ag–0.4Zr alloy

Microstructure and mechanical properties of hot-rolled Mg–Zn–Nd–Zr alloys

Microstructure and Mechanical Properties of Mg–3.0Y–2.5Nd–1.0Gd–x Zn–0.5Zr Alloys Produced by Metallic and Sand Mold Casting