Dynamic Deformation Behavior of a Face-Centered Cubic FeCoNiCrMn High-Entropy Alloy.

Junyang He,Qi Wang,Husheng Zhang,Lanhong Dai,Toshiji Mukai,Yuan Wu,Xiongjun Liu,Hui Wang,Tai-Gang Nieh,Zhaoping Lu
DOI: https://doi.org/10.1016/j.scib.2018.01.022
IF: 18.9
2018-01-01
Science Bulletin
Abstract:In this study, mechanical tests were conducted on a face-centered cubic FeCoNiCrMn high-entropy alloy, both in tension and compression, in a wide range of strain rates (10(-4)-10(4) s(-1)) to systematically investigate its dynamic response and underlying deformation mechanism. Materials with different grain sizes were tested to understand the effect of grain size, thus grain boundary volume, on the mechanical properties. Microstructures of various samples both before and after deformation were examined using electron backscatter diffraction and transmission electron microscopy. The dislocation structure as well as deformation-induced twins were analyzed and correlated with the measured mechanical properties. Plastic stability during tension of the current high-entropy alloy (HEA), in particular, at dynamic strain rates, was discussed in lights of strain-rate sensitivity and work hardening rate. It was found that, under dynamic conditions, the strength and uniform ductility increased simultaneously as a result of the massive formation of deformation twins. Specifically, an ultimate tensile strength of 734 MPa and uniform elongation of similar to 63% are obtained at 2.3 x 10(3) s(-1), indicating that the alloy has great potential for energy absorption upon impact loading. (C) 2018 Science China Press. Published by Elsevier B.V. and Science China Press. All rights reserved.
What problem does this paper attempt to address?