Abstract:The fabrication of TiO2 nanotube arrays (TNTs) by the anodization of titanium foil in electrolyte containing fluoride was carried out in this study. The surface dimension, phase formation, and lattice parameters of TNTs were determined by the field-emission-scanning electron microscopy and X-ray diffractometer, respectively. The induced photocurrent intensity of TNTs was measured by a potentiostat/galvanostat. The well-defined and highly ordered TNTs were formed in glycerol electrolyte with a water content of 20%. The inner diameter of the TNTs was mainly determined by the anodization voltage, while the length of the TNTs was affected by both anodization voltage and anodization time. The length of the nanotube was continually increased with anodization time until the rates of the electrochemical oxidization of Ti foil and the chemical dissolution of the TiO2 film reached a dynamic equilibrium. The TNTs annealed at 600 degrees C demonstrated the highest induced photocurrent because of the crystallization of anatase and rutile phases. The increase in the tube length and the decrease in the inner diameter induced higher photocurrents under specific conditions of UV illumination because of a higher illuminated area. However, the enhancement of the induced photocurrent was retarded when the length of the TNTs reached 2000 nm due to the limited penetration of incident UV light penetrated through the nanotube. (C) 2010 The Electrochemical Society. [DOI: 10.1149/1.3384659] All rights reserved.

Photoelectrochemical Properties of N Doped Black TiO2 Nanotube Arrays

Photoelectrochemical Property and Photocatalytic Activity of N-doped TiO2 Nanotube Arrays

Nitrogen-Doped Tio2 Nanotube Arrays With Enhanced Photoelectrochemical Property

Nitrogen-Doped TiO<sub><b>2</b></sub>Nanotube Arrays with Enhanced Photoelectrochemical Property

Photoelectrical properties of nitrogen doped TiO 2 nanotubes by anodic oxidation of N + implanted Ti foils

Preparation and Photoelectrochemical Properties of Nitrogen Doped Nanotubular TiO2 Arrays

N-doped TiO2 Nanotube Array Photoelectrode for Visible-Light-induced Photoelectrochemical and Photoelectrocatalytic Activities

Electrochemically Self-Doped Hierarchical Tio2 Nanotube Arrays For Enhanced Visible-Light Photoelectrochemical Performance: An Experimental And Computational Study

Time-dependent Formation of Oxygen Vacancies in Black TiO2 Nanotube Arrays and the Effect on Photoelectrocatalytic and Photoelectrochemical Properties

Synthesis of Cu,N-Doped TiO<sub>2</sub> Nanotube and Study on Photoelectric Properties

Electrochemically Induced Ti3+ Self-Doping of TiO2 Nanotube Arrays for Improved Photoelectrochemical Water Splitting

Effective photocatalytic properties of N doped Titanium dioxide nanotube arrays prepared by anodization

Enhanced Photoelectrocatalytic Degradation of Organic Pollutants Using TiO2 Nanotubes Implanted with Nitrogen Ions

Enhanced Photoelectrochemical Property of Zn Loaded TiO2 Nanotube Arrays Electrode

Enhanced Visible Light Photoelectrochemical Performances with Nitrogen Doped TiO_2 Nanowire Arrays

Characterization and Induced Photocurrent of TiO[sub 2] Nanotube Arrays Fabricated by Anodization

A Photoelectrochemical Investigation of the Hydrogen-Evolving Doped TiO2 Nanotube Arrays Electrode

Enhanced Photoelectrochemical Performance and Charge Transfer Properties in Self-Organized NiOx-doped TiO2 Nanotubes

Enhanced Photoelectrochemical Properties of TiO2 Nanotube Arrays Sensitized with Energy-Band Tunable (cu2sn)x/3zn1−xs Nanoparticles

Photoelectrical and Charge Transfer Properties of Hydrogen-Evolving TiO2 Nanotube Arrays Electrodes Annealed in Different Gases