Abstract:Powder bed fusion (PBF) is an additive manufacturing technique capable of fabricating highly complex, individualised, and lightweight polymer components. However, to maximise the potential of PBF, in terms of both economic efficiency and environmental sustainability, a successful powder re-use strategy is essential. During a build, ageing and degradation processes affect the re-usability of un-sintered powder, so used powder is usually refreshed with virgin material before re-use. This study considers the effectiveness of using a 70:30 refresh ratio in a specific PBF technique: laser sintering (LS). Across a total of seven printing cycles, polyamide-12 (PA-12) powder refreshed with 30% virgin material after each build, revealed a 4.5°C increase in melting temperature. There was also a 20% reduction in particle flowability, which may be related to the presence of fine satellite particles and considerable particle cracking. This deterioration in powder quality resulted in a 5.8% increase in total part porosity, and an 11% reduction in the ultimate tensile strength of fabricated parts, over the seven build cycles. A Pearson correlation test quantified that the reduction in powder flowability was the most significant (p-value of 0.005) cause for the loss of part strength; emphasising that the revolution powder analyser could be a useful complimentary technique for determining the quality of used powder within laser sintering. Nonetheless, compared to previous studies which re-used 100% aged PA-12 powder, without refreshing with any virgin material, the observed reduction in part strength is relatively modest. This suggests that a 70:30 refresh ratio offers a good compromise between maintaining part performance, particularly for non-critical applications, without having to add an unnecessary amount of virgin powder. Therefore, this study reveals the relationship between the deterioration of powder properties and reductions in part strength; yet highlights the benefits of operating with a 70:30 refresh ratio when re-using PA-12 powder across multiple build cycles.

Systematical Mechanism of Polyamide-12 Aging and Its Micro-Structural Evolution During Laser Sintering

Effects of laser sintering processing time and temperature on changes in polyamide 12 powder particle size, shape and distribution

Aging mechanism of polyetheretherketone powder during layer-wise infrared radiation of high-temperature laser powder bed fusion

Towards the Reuse of Fire Retarded Polyamide 12 for Laser Sintering

Investigation of the ageing conditions of PEEK powder for the selective laser sintering process

Experimental investigating and numerical simulations of the thermal behavior and process optimization for selective laser sintering of PA6

On the Difference in Mechanical Behavior of Glass Bead-Filled Polyamide 12 Specimens Produced by Laser Sintering and Injection Molding

Insights into the effects of epoxy resin infiltration on powder aging issue induced by powder recycling in powder bed fusion of Nylon12 materials

Predictive Modeling of Mechanical Properties from Degraded Polyamide 12 Powder in Laser Powder Bed Fusion

Experimental Characterization and Strengthening Mechanism of Process-Structure-property of Selective Laser Melted 316 L

Process-structure-property Modeling for Postbuild Heat Treatment of Powder Bed Fusion Ti-6Al-4V

Effects of Physical Aging on Thermomechanical Behaviors of Poly(ethylene Terephthalate)-Glycol (PETG)

A large compressive recoverable strain induced by heterogeneous microstructure in a Ni50.6Ti49.4 shape memory alloy via laser powder bed fusion and subsequent aging treatment

Superstrengthening Effect of Beyond-Solid-Solution Laser Powder Bed Fused We43 Magnesium Alloy Triggered by Direct Aging Treatment

Re-use of polyamide-12 in powder bed fusion and its effect on process-relevant powder characteristics and final part properties

Optimization of Mechanical Properties and Evaluation of Fatigue Behavior of Selective Laser Sintered Polyamide-12 Components

Effect of Solution and Single-Stage Aging on Microstructural Evolution and Mechanical Properties of Inconel 718 Alloy Manufactured by Selective Laser Melting

The Effect of Powder Re-Use on the Coalescence Behaviour and Isothermal Crystallisation Kinetics of Polyamide 12 within Powder Bed Fusion

Influence of Aging Treatment Regimes on Microstructure and Mechanical Properties of Selective Laser Melted 17-4 PH Steel

Evolution of thermal behavior, mechanical properties, and microstructure in stereocomplexable poly(lactic acid) during physical ageing