Abstract:Electrochemical CO 2 reduction reaction (CO 2 RR) to HCOOH is one of the most feasible and economical methods to achieve carbon neutrality. Bismuth (Bi), as a metal catalyst for CO 2 RR, is considered to have great potential for application and has been widely studied due to its high formate selectivity, low toxicity, cheapness, and abundance. Unfortunately, low current density and short electrode lifetime have hindered its progress towards practical applications. In this work, we present a method that enables the chemical etching of Bi on Cu, which is capable of spontaneously accomplishing the loading of Bi on Cu foam in the liquid phase at room temperature. Additionally, to provide more abundant catalytically active sites, twisted Bi nanowires (BiNWs) with lattice dislocations were successfully prepared on the surface of Cu foam using a three-step chemical method involving oxidation, reduction, and in-situ etching. The Cu Foam@BiNWs was found to be a highly active electrocatalyst for CO 2 reduction to formate at a low applied potential, achieving a faradaic efficiency for formate (FE Formate ) of 95 % and a formate partial current density of ∼ 12 mA cm −2 at −0.78 V vs. RHE (reversible hydrogen electrode). Even within such a wide potential window of −0.68 ∼ -1.08 V vs. RHE, the FE Formate is consistently above 90 %. Such exceptional CO 2 reduction activity can be attributed to the distortions and lattice dislocations present in the surface BiNWs. Furthermore, the Cu Foam@BiNWs electrode demonstrated a total current density close to 100 mA cm −2 at −0.98 V in an alkaline flow cell, while maintaining excellent catalytic stability over a prolonged 30-hour period of high current density electrochemical activity, thus showing potential for advancing the industrialisation of formate production. This work emphasizes the crucial role of size-dependent catalysis and crystal defect engineering strategies in the field of electrocatalysis, elucidates the mechanism of the rate-determining step (RDS) in the electrocatalytic CO 2 reduction process on the developed catalysts, which can provide valuable insights into the design and development of high performance electrocatalysts not only in CO 2 RR but also in other fields.

Electrochemical Reduction of CO2 on Defect-Rich Bi Derived from Bi2S3 with Enhanced Formate Selectivity

Synthesis of Few-Layer Bismuthene for Efficient Electroreduction of CO 2 to Formate

Defect-rich bismuth metallene for efficient CO2 electroconversion

Ultrathin Bismuth Nanosheets as a Highly Efficient CO2 Reduction Electrocatalyst

Sn-Doped Bi2O3 Nanosheets for Highly Efficient Electrochemical CO2 Reduction Toward Formate Production.

High current CO2 reduction realized by edge/defect-rich bismuth nanosheets

Bismuth with abundant defects for electrocatalytic CO 2 reduction and Zn–CO 2 batteries

Bismuth Iron Oxide Catalysts for Efficient CO2 Electroreduction to Formate

Structural defects on converted bismuth oxide nanotubes enable highly active electrocatalysis of carbon dioxide reduction

Lattice-dislocated bismuth nanowires formed by in-situ chemical etching on copper foam for enhanced electrocatalytic CO 2 reduction

Bismuth Oxides with Enhanced Bismuth–Oxygen Structure for Efficient Electrochemical Reduction of Carbon Dioxide to Formate

In-situ electrochemical restructuring of Cu2BiSx solid solution into Bi/CuxSy heterointerfaces enabling stabilization intermediates for high-performance CO2 electroreduction to formate

Synergistic Geometric and Electronic Effects in Bi–Cu Bimetallic Catalysts for CO 2 Electroreduction to Formate over a Wide Potential Window

High Throughput Preparation of Bi-Sb Alloy Films for the Electrocatalytic Reduction of CO 2 to Formate

Perovskite‐Derived Bismuth with I− and Cs+ Dual Modification for High‐Efficiency CO2‐to‐Formate Electrosynthesis and Al‐CO2 Batteries

Promoting Electrochemical CO2 Reduction to Formate via Sulfur‐Assisted Electrolysis

Ampere-level CO2-to-formate electrosynthesis using highly exposed bismuth(110) facets modified with sulfur-anchored sodium cations

Bismuth oxide nanoflakes grown on defective microporous carbon endows high-efficient CO2 reduction at ampere level

Perovskite-Derived Bismuth with I<SUP>-</SUP> and Cs<SUP>+</SUP> Dual Modification for High-Efficiency CO<sub>2</sub>-to-Formate Electrosynthesis and Al-CO<sub>2</sub> Batteries

Electronic Delocalization of Bismuth Oxide Induced by Sulfur Doping for Efficient CO 2 Electroreduction to Formate

Bismuth Single Atoms Resulting from Transformation of Metal-Organic Frameworks and Their Use As Electrocatalysts for CO2 Reduction.