Microstructure, Texture, and Mechanical Properties of As-Extruded Mg-xLi-3Al-2Zn-0.2Zr Alloys (x = 5, 7, 8, 9, 11 Wt%)
Yuehua Sun,Richu Wang,Jian Ren,Chaoqun Peng,Zhiyong Cai
DOI: https://doi.org/10.1016/j.msea.2019.04.007
IF: 6.044
2019-01-01
Materials Science and Engineering A
Abstract:The microstructure, texture, and mechanical properties of as-extruded Mg-xLi-3Al-2Zn-0.2Zr alloys (x = 5, 7, 8, 9, 11 wt%) were investigated. After hot extrusion, the filamentous AlLi phase in alpha-Mg is crushed into tiny particles, while the morphology of round-like AlLi phase in beta-Li remains unchanged. The threadlike MgLi2Al phase precipitated during hot extrusion only distributes along the grain boundaries of beta-Li phase. The grains of as-extruded alloys are refined markedly due to dynamic recrystallization (DRX), and alpha-Mg phase undergoes discontinuous DRX while beta-Li phase undergoes continuous DRX. The {0001} basal, {10 (1) over bar0} and {11 (2) over bar0} prismatic fiber textures formed in alpha-Mg phase suggest the activation of both basal and prismatic slip, and the intensity of prismatic texture is higher than that of basal texture. In beta-Li phase, as the extrusion temperature increases and the Li content decreases, the intensities of alpha fiber and {110}110 textures decrease while those of gamma fiber and {110}//ED textures increase. Compared with as-homogenized alloys, the mechanical properties of as-extruded alloys are significantly improved owing to grain refinement strengthening, texture hardening, strain hardening, and second phase strengthening.