Abstract:It is a great challenge to fabricate superwetting catalytic membranes with intrinsic self-cleaning capacity for highly stable and effective water purification by simple, mild and energy-efficient manufacturing technologies. Herein, diffusion-induced interfacial self-assembly and polyphenol-mediated strengthening strategies were employed to fabricate tannic acid -mediated layered double hydroxide hybridizing PVDF superwetting catalytic membranes (named as TA@CoFe-LDH@PVDF). The simultaneous phase transformation/in-situ synthesis of CoFe-LDH nanosheets and subsequent coordination assembly with tannic acid (TA) was implemented. Superhydrophilic and underwater-superoleophobic properties were achieved through the cooperation effect of the rough microstructures of CoFe-LDH nanosheets and the strong hydration ability of TA molecules. This enabled efficient separation of various oil-in-water emulsions with more than 99 % separation efficiency and permeation flux up to 593.9 L m-2h-1 bar- 1 in cross-flow filtration. Furthermore, due to the reducibility of TA molecules that promoted the Mn+1/Mn+cycle, TA@CoFe-LDH@PVDF membrane exhibited high static degradation efficiency and kinetics (nearly 100 % in 5.0 min) toward methylene blue by PMS activation. The degradation rate constant (1.04 min- 1) was 2.67 times compared to that of CoFe-LDH@PVDF. Surprisingly, it was found that the dynamic mass transfer process in the membrane significantly accelerated the catalytic kinetics, resulting in a degradation rate in dead-end filtration was 23.89 times higher than that under static conditions. Additionally, it was proved that assembled TA could inhibit and reduce metal ion leaching during the catalytic and separation process. This simple manufacturing process of multifunctional membranes with superior performances offers a high application potential in wastewater treatment.

Surface modification to produce superhydrophobic hollow fiber membrane contactor to avoid membrane wetting for biogas purification under pressurized conditions

Fabrication of High-Flux PTFE Hollow Fiber Membranes Through Nonionic Surfactant Infiltration Coupled with Mussel-Inspired Chemistry Coating

Preparation and Modification of Ceramic Membrane and Its Application in Oil/Water Wastewater Treatment

Fabrication and Characterization of Poly(vinylidene Fluoride)–polytetrafluoroethylene Composite Membrane for CO2 Absorption in Gas–liquid Contacting Process

Fabrication of a super hydrophobic polyvinylidene fluoride–hexadecyltrimethoxysilane hybrid membrane for carbon dioxide absorption in a membrane contactor

Tannic Acid-Mediated Layered Double Hydroxide Hybridizing PVDF Superwetting Catalytic Membranes Constructed Via Ion Diffusion-Induced Interfacial Self-Assembly for Boosting Water Purification

Developing PVDF Hollow Fiber Membrane Enhanced by Braided Tube and Modified by Bionic Coating for Treating Aldehyde-Containing Wastewater

Fabrication of a superhydrophobic mixed matrix PVDF-SiO2-HDTMS hollow fiber membrane for membrane contact carbon dioxide absorption

Long-term stability of PVDF-SiO2-HDTMS composite hollow fiber membrane for carbon dioxide absorption in gas–liquid contacting process

Fabrication of superhydrophobic PVDF membrane via catechol/polyamine co-deposition and SiO 2 nanoparticles for membrane distillation

Effect of polytetrafluoroethylene hollow fiber microstructure on formaldehyde carbonylation performance in membrane contactor

Preparation of a novel dual-layer polyvinylidene fluoride hollow fiber composite membrane with hydrophobic inner layer for carbon dioxide absorption in a membrane contactor

Surface modification of polypropylene hollow fiber membranes using fluorosilane for CO2 absorption in a gas-liquid membrane contactor

Robust superwetting polytetrafluoroethylene membranes with interlayer-bridged inorganic nanocoating for efficient oil/water separation

Enhancing membrane wetting resistance through superhydrophobic modification by polydimethylsilane-grafted-SiO2 nanoparticles

Slippery hydrogel surface on PTFE hollow fiber membranes for sustainable emulsion separation

Fabrication of Tween-20 Coated PVDF Membranes for Wastewater Treatment: Optimization of Preparation Parameters, Removal and Membrane Fouling Control Performance

Surface modification of polypropylene microporous membrane to improve its antifouling property in MBR: CO2 plasma treatment

Preparation and characterization of superhydrophobic PVDF/HMSNs hybrid membrane for CO<sub>2</sub> absorption

Silanization enabled superhydrophobic PTFE membrane with antiwetting and antifouling properties for robust membrane distillation

Fabrication of Sub-Tg Cross-Linked and Thermally Rearranged Poly (Benzoxazole-Co-imide) Hollow Fiber Membrane Derived from Phenolphthalein-Based Copolyimide for CO2/CH4 Separation