Superhydrophobic Surface-Constructed Membrane Contactor with Hierarchical Lotus-Leaf-Like Interfaces for Efficient SO 2 Capture
Qingping Xin,Xu Li,Hailong Hou,Qingqing Liang,Jianping Guo,Shaofei Wang,Lei Zhang,Ligang Lin,Hui Ye,Yuzhong Zhang
DOI: https://doi.org/10.1021/acsami.0c17534
2020-12-31
Abstract:An organic–inorganic polyvinylidene fluoride/polyvinylidene fluoride–silica (PVDF/PVDF-SiO<sub>2</sub>) mixed matrix membrane contactor is fabricated via a facile and efficient hydrophobic modification method. The solubility parameters of the PVDF particle are precisely regulated, the PVDF particles are blended with SiO<sub>2</sub> nanoparticles to form PVDF-SiO<sub>2</sub> suspension, and then the suspension is introduced onto the surface of the PVDF substrate by an <i>in situ</i> spin coating strategy. The PVDF particles are partly etched and incorporated to construct the adhesive PVDF-SiO<sub>2</sub> core–shell layer on the PVDF substrate, which results in a more stable PVDF-SiO<sub>2</sub> coating layer on the substrate. The surface structure is precisely regulated by changing the etching morphology of PVDF particles and amount of doped PVDF and SiO<sub>2</sub> particles, forming an integrated porous PVDF-SiO<sub>2</sub> layer and constructing hierarchical lotus-leaf-like interfaces. The resultant PVDF/PVDF-SiO<sub>2</sub> membrane contactors display the relatively regular distribution of pore size with ∼420 nm and excellent hydrophobic property with a water contact angle of ∼158°, which noticeably lightens wetting phenomena of membrane contactors. The SO<sub>2</sub> absorption fluxes can reach as high as 1.26 × 10<sup>–3</sup> mol·m<sup>–2</sup>·s<sup>–1</sup> using 0.625 M of ethanolamine (EA) as liquid absorbent. The high stability of the SO<sub>2</sub> absorption flux test indicates the excellent interface compatibility between the PVDF-SiO<sub>2</sub> coating layer and the PVDF substrate. The versatile organic–inorganic layer exhibits super hydrophobic property, which prevents wetting of membrane pores. In addition, the membrane mass transfer resistance (<i>H</i>/<i>K</i><sub>m</sub>) and membrane phase transfer coefficient (<i>K</i><sub>m</sub>) are explored.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c17534?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c17534</a>.Measurement of (HOCH<sub>2</sub>CH<sub>2</sub>NH<sub>3</sub>)<sub>2</sub>SO<sub>3</sub> solubility; detailed description of the SO<sub>2</sub> absorption removal process; TEM characterizations of SiO<sub>2</sub> and pristine PVDF particles; SEM images of PVDF/PVDF-SiO<sub>2</sub> MMMCs; all the measured pictures of WCA data for membrane contactors; SEM image of the M<sub>1</sub><sup>100</sup> membrane contactor after SO<sub>2</sub> removal; and the relationships between SO<sub>2</sub> absorption flux and LEP; SO<sub>2</sub> removal efficiency and surface roughness ; influence of membrane thickness on SO<sub>2</sub> absorption flux (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c17534/suppl_file/am0c17534_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology