Abstract:Ca-doped lithium titanates with the formula of Li4-xCaxTi5O12 (x= 0, 0.05, 0.1, 0.15, 0.2) were synthesized as anode materials by a simple solid-state reaction in an air atmosphere. The phase structure, morphologies and electrochemical properties of the prepared powders were systematically characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and cyclic voltammetry (CV), respectively. XRD revealed that the Ca-doping caused no change on the phase structure and highly crystalline Li4-xCaxTi5O12 (0 <= x <= 0.2) powders without any impurity were obtained. SEM images sfiowed that all samples had similar particulate morphologies and the particle size distribution was in the range of 1-2 mu m. It was observed that Ca-doped lithium titanates employed as the anode materials of lithium-ion batteries delivered excellent electrochemical performances, and sample Li3.9Ca0.1Ti5O12 exhibited a higher specific capacity, better cycling performance and rate capability than other samples. The Li3.9Ca0.1Ti5O12 material showed discharge capacities of 162.4 mAh g(-1), 148.8 mAh g(-1) and 138.7 mAh g(-1) after 100 cycles at 1 C, 5C and 10 C charge-discharge rates, respectively. Electrochemical impedance spectroscopy (EIS) revealed that the Li3.9Ca0.1Ti5O12 electrode exhibited the highest electronic conductivity and fastest lithium-ion diffusivity, which indicated that this novel Li3.9Ca0.1Ti5O12 material was promising as a high-rate anode material for the lithium-ion batteries. (C) 2013 Elsevier Ltd. All rights reserved.

Synthesis of Carbon-Coated Li 4 Ti 5 O 12 and Its Electrochemical Performance As Anode Material for Lithium-Ion Battery

Facile Synthesis and Characterization of Li4Ti5O12 As Anode Material for Lithium Ion Batteries

Li4Ti5O12 Prepared by a Modified Citric Acid Sol–gel Method for Lithium-Ion Battery

Structural Analysis and Electrochemical Studies of Carbon Coated Li4ti5o12 Particles Used As Anode for Lithium Ion Battery

Mechanochemical Synthesis and Electrochemical Performances of Li4Ti5O12 Anode Materials for Lithium Ion Batteries

Mechanochemical Synthesis and Electrochemical Performances of Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub> Anode Materials for Lithium Ion Batteries

Structure and Performance of Lithium Battery Anode Material Li4Ti5O12

Synthesis of Carbon-Coated Li3VO4 and Its High Electrochemical Performance As Anode Material for Lithium-Ion Batteries

Synthesis of sawtooth-like Li4Ti5O12 nanosheets as anode materials for Li-ion batteries

Synthesis of nano-sized Li 4Ti 5O 12/C composite anode material with excellent high-rate performance

Synthesis And Electrochemical Properties Of Li4ti5o12/Cuo Anode Material For Li-Ion Batteries

Enhanced Electrochemical Performance of Li4Ti5O12 As Anode Material for Lithium-Ion Batteries with Different Carbons As Support

Facile Preparation of Nanocrystalline Li4Ti5O12 and Its High Electrochemical Performance As Anode Material for Lithium-Ion Batteries

A Simple Gel Route to Synthesize Nano-Li 4 Ti 5 O 12 As a High-Performance Anode Material for Li-ion Batteries

Nano-Li4Ti5O12 with High Rate Performance Synthesized by a Glycerol Assisted Hydrothermal Method

Enhanced Electrochemical Performance of a Novel Li4Ti5O12 Composite As Anode Material for Lithium-Ion Battery in a Broad Voltage Window

Solid-State Synthesis of Graphite Carbon-Coated Li4ti5o12 Anode for Lithium Ion Batteries

Preparation and Characterization of Porous Spherical Li_4Ti_5O_(12)/C Anode Material for Lithium Ion Batteries

In Situ Synthesis of Carbon Incorporated Tio2 with Long-Term Performance As Anode for Lithium-Ion Batteries

Synthesis and Electrochemical Properties of Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub>/CuO Anode Material for Li-Ion Batteries

Preparation and Electrochemical Properties of Ca-doped Li4Ti5O12 As Anode Materials in Lithium-Ion Battery