Effect Of Cold Rolling Before Hydrogen Reduction On Reduction Behavior And Morphologies Of Oxide Scale On Hot-Rolled Low-Carbon Steel

Zhi-feng Li,Guangming Cao,Fei Lin,Xianzhen Sun,Yong-quan He,Zhenyu Liu

DOI: https://doi.org/10.2355/isijinternational.ISIJINT-2017-266

2017-01-01

ISIJ International

Abstract:A new 'acid-free picking' method that adding cold rolling prior to hydrogen-reduction descaling was put forward in this study. The purpose of cold rolling was to break the completeness of oxide scale and increase reduction efficiency. Subsequently, the high-temperature reduction behavior of oxide scale on the surface of hot-rolled low carbon steel, which reacted with hydrogen after 10% deformation of cold rolling in 20%H-2-Ar at the temperature range of 400-850 degrees C, was investigated to validate the feasibility. The mass loss of specimens in the non-isothermal and isothermal reduction experiment was clearly measured by thermogravimetric analysis (TGA). Scanning electron microscopy (SEM) was used to observe surface morphology and cross-section microstructure of reduction products. The phase composition of reduction products was identified by X-ray diffraction (XRD). The experimental results indicated that the reduction reaction degree can be controlled by three main factors: reduction temperature, time and cold rolling. After 10% deformation of cold rolling, the completeness of original oxide scale was broken and then a large amount of micro-cracking appeared in oxide scale and the gap formed at oxide/substrate interface. The reduction rate of broken oxide scale was significantly faster than that of original oxide scale when the reduction temperature achieved more than 700 degrees C. The effect of micro-cracking and gap on the mechanism of reduction process were clarified based on reaction of gas (H-2)-solid (iron oxides) interface.