Abstract:Edge cracks are a type of damage that critically affect the quality and properties of rolled Mg alloys sheet. Accurate damage prediction plays a key role in root cause analysis and process optimization. Although the phenomenological prediction of edge damage in Mg alloy rolling has made some progress so far, the prediction of edge crack behavior and analysis of the mechanisms of crack formation and evolution during rolling have not yet been well reported. In this research, a modified Gurson-Tvergarrd-Needleman (GTN) model was proposed by modifying the growth mode of shear damage. The three-dimensional single-unit finite element (FE) model test results indicated that the proposed model improved the accuracy of the fracture response under negative stress triaxiality. Using AZ31B Mg alloy as the case study material, physical experiments and FE analysis of the rolling process were conducted. The simulations showed that the proposed model can accurately reflect the morphology and location of cracks during the rolling process, and revealed that the high-stress triaxiality at the Mg alloy edge was a significant cause of edge cracking. On this basis, an edge-constraint rolling process was proposed to inhibit edge cracking by embedding the billet into a U-shaped sheet. The numerical results showed that the minimum value of edge stress triaxiality could be reduced from -0.8 to -2.05 during edge-constraint rolling, and the accumulation of damage could be limited. The sheet forming quality was verified with different reduction rates of 30, 35, and 40 %, and the results showed that the edge cracks could be effectively avoided during edge-constraint rolling, which provides an important basis for optimizing the rolling deformation process of Mg alloys.

Application of the XFEM to Predict the Edge Crack Propagation of Steel Sheet in the Cold Rolling Process

Predicting of Edge Crack Behavior of Steel Sheet in the Cold Rolling Process Based on Cohesive Zone Model

Application of the Cohesive Zone Model for Analysing the Edge Crack Propagation of Steel Sheet in the Cold Rolling Process

Simulation Of Crack Propagation In Asphalt Concrete Pavement At Low Temperature Using Extended Finite Element Method

A New Ductile Fracture Model for Edge Cracking Prediction of Ultra-High Strength Steel Considering Damage Accumulation in Blanking Process

Prediction of magnesium alloy edge crack in edge-constraint rolling process by using a modified GTN model

Numerical Analysis of Edge Cracking in High-Silicon Steel during Cold Rolling with 3D Fracture Locus

Numerical Simulation on Edge Crack of Advanced High-Strength Steel Considering Blanking Induced Damage

Finite Element Analysis of Temper Rolling Process

Fracture prediction of high-strength steel sheet during in-plane compression-shear forming under negative stress triaxiality

Theoretical Study of Asymmetric Bending Force on Metal Deformation in Cold Rolling

Steel Edge Cracking Analysis and Improvement Measures

Experiments and FE Simulation of Edge Cracking Considering Prehardening after Blanking Process

Fracture prediction for metal sheet deformation under different stress states with uncoupled ductile fracture criteria

Ductile Fracture Modeling of Initiation and Propagation in Sheet-Metal Blanking Processes

A Novel Method for Residual Strength Prediction for Sheets with Multiple Site Damage: Methodology and Experimental Validation

Study of Curvature and Pre-Damage Effects on the Edge Stretchability of Advanced High Strength Steel Based on a New Simulation Model

The Numerical Simulation and Failure Prediction for Thick Sheet Metal Fine-Blanking Based on Oyane Damage and Fracture Model

Influence of Sheet Metal Pre-forming on Edge Crack Sensitivity using an AHSS Steel Grade

Model for predicting ductile fracture of SA508-3 steel undergoing hot forming

Effect of Residual Stress on Fatigue Behaviour of Notches