Abstract:Using the Raney Fe-Al alloy as the precursor for Fe and Al, and tetrapropylammonium hydroxide (TPAOH) as both the base for the leaching of the alloy and the template for the synthesis of HZSM-5, we synthesized the skeletal Fe core-HZSM-5 shell catalysts (Raney Fe@HZSM-5) via a facile one-pot hydrothermal strategy. The thickness of the zeolite shell was adjusted by varying the hydrothermal time. The catalysts were characterized by inductively coupled plasma-atomic emission spectroscopy (ICP-AES), N-2 physisorption, X-ray powder diffraction (XRD), temperature-programmed desorption of NH3 (NH3-TPD), and scanning electron microscopy (SEM). It was identified that the Raney Fe-Al alloy was more suitable than the rapidly quenched Fe-Al alloy as the precursor to the skeletal Fe core, since the skeletal Fe catalyst alkali-leached from the former produced more long-chain hydrocarbons during the Fischer-Tropsch synthesis (FTS) reaction for successive cracking and isomerization. A complete HZSM-5 shell was obtained only after above 24 h of hydrothermal treatment. With the hydrothermal time from 2 d to 8 d, the thickness of the compact HZSM-5 shell increased from 1.3 mu m to 9.7 mu m, the relative crystallinity increased steadily, while the SiO2/Al2O3 ratio remained essentially constant, and the amount of the acid sites is parallel to the thickness of the zeolite shell. In the FTS reaction using syngas with the H-2/CO molar ratio of 2 and at 543 and 2.0 MPa, the CO conversion and the selectivity to the gasoline fraction (C-5 similar to C-11 hydrocarbons) evolved in a volcanic trend with the shell thickness, suggesting the existence of an optimal amount of the acid sites, while less or more is adverse to the activity and selectivity to the gasoline fraction. The Raney Fe@HZSM-5 catalyst hydrothermally treated for 4 d exhibited the highest CO conversion of 92% and the selectivity to the gasoline fraction of 71%, along with an iso-paraffin to n-paraffin ratio of 1.9. At the n(H-2)/n(CO) ratio of 1, the selectivity to the gasoline fraction and the iso-paraffin to n-paraffin ratio were further improved to 73% and 2.1, respectively, which shows promise for this catalyst to transform the coal- or biomass-derived syngas to high-octane number gasoline.

Microfibrous-structured Hollow-Zsm-5/ss-fiber Catalyst with Mesoporosity Development Dependent Lifetime Improvement for MTP Reaction

Methanol to Propylene over Foam SiC-Supported ZSM-5 Catalyst: Performance of Multiple Reaction–Regeneration Cycles

Pore Plugging Effects on the Performance of ZSM-5 Catalyst in MTP Reaction Using a Discrete Model

Si/Al Ratio Induced Structure Evolution During Desilication-Recrystallization of Silicalite-1 to Synthesize Nano-Zsm-5 Catalyst for MTH Reaction

High-silica hierarchical ZSM-5 prepared by conventional alkali treatment: A highly stable MTP catalyst

Core–shell Structured Catalyst of HZSM-5 Zeolite Supported on Stainless Steel Fiber for Methanol-to-aromatics

Synthesis of hollow HZSM-5 zeolite-based catalysts and catalytic performance in MTA reaction

ZSM-5@MCM-41 core–shell composite with tunable shell thickness for n -heptane catalytic cracking reaction

High Throughput Research and Development of Catalysts for Converting Methanol into Propylene

Silicalite-1 Derivational Desilication-Recrystallization to Prepare Hollow Nano-ZSM-5 and Highly Mesoporous Micro-ZSM-5 Catalyst for Methanol to Hydrocarbons

Organosilane Surfactant-Assisted Synthesis of Mesoporous SSZ-39 Zeolite with Enhanced Catalytic Performance in the Methanol-to-olefins Reaction

Effect of Shell Thickness on Skeletal Fe@HZSM-5 Core-Shell Catalysts for Fischer-Tropsch Synthesis

Solvent-free and Mesoporogen-free Synthesis of Mesoporous Aluminosilicate ZSM-5 Zeolites with Superior Catalytic Properties in the Methanol-to-Olefins Reaction

Fabrication of Twin-Free Nanoslab ZSM-5 Zeolite with b -Axis Orientation for Super MTP Catalyst

Synthesis of ZSM-5 Catalysts with Tunable Mesoporosity by Ultrasound-Assisted Method: A Highly Stable Catalyst for Methanol to Propylene

Simultaneous Enhancement of Aromatic Products and Catalytic Lifetime for Catalytic Re-forming of Lignite Pyrolysis Volatiles over a Self-Assembled Hierarchical Core–Shell ZSM-5@Silicalite-1 Zeolite

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

Hierarchically Tetramodal-Porous Zeolite ZSM-5 Monoliths with Template-Free-derived Intracrystalline Mesopores

In-situ synthesis of hierarchical lamellar ZSM-5 zeolite with enhanced MTP catalytic performance by a facile seed-assisted method

Hierarchical ZSM-5 zeolite designed by combining desilication and dealumination with related study of n-heptane cracking performance

Full-crystalline Hierarchical Monolithic ZSM-5 Zeolites As Superiorly Active and Long-Lived Practical Catalysts in Methanol-to-hydrocarbons Reaction