Abstract:A series of core -shell zeolites with a ZSM-5 zeolite core and a MCM-41 shell with varying shell thicknesses were successfully fabricated via a cetyltrimethylammonium bromide (CTAB)-directed sol-gel coating method in an ultradilute solution. Extensive characterization techniques, including XRD, TEM, N2 adsorption -desorption, NH3-TPD, and IR measurements, confirmed the successful coating of a microporous ZSM-5 core with a mesoporous MCM-41 shell layer and were further employed to explore the textural properties and acidic properties of the samples. The hexane cracking results revealed a significant enhancement in olefin yields after introducing the MCM-41 shell to ZSM-5. Interestingly, a volcanic trend in olefin yields was observed with the increase in the shell thickness. In particular, the highest olefin yield of 51.5%, exceeding that of the core catalyst by 17.1%, was achieved when the shell thickness was controlled at 40 nm. Moreover, the catalyst lifetime investigation revealed that the core -shell composite catalyst exhibited a minimal reduction in hexane conversion of merely 3.8% over a 120 h reaction period, significantly outperforming the 11.3% reduction exhibited by the core catalyst. This remarkable catalytic performance was attributed to the passivation of external acid sites and the introduction of more developed pore channels by the shell, which effectively mitigated unwanted side reactions. The successful synthesis of these core -shell structured catalysts presents a novel strategy for improving catalytic performance in hexane cracking, in addition to serving as a solid foundation for the design of industrial catalysts for light naphtha cracking.

Core–shell Structured Catalyst of HZSM-5 Zeolite Supported on Stainless Steel Fiber for Methanol-to-aromatics

Synthesis and Physicochemical Characterization of Hierarchical ZSM-5: Effect of Organosilanes on the Catalyst Properties and Performance in the Catalytic Fast Pyrolysis of Biomass

Enhanced Catalytic Performance of Hierarchical Zn/ZSM-5 with Balanced Acidities Synthesized Utilizing ZIF-14 As Porogen and Zn Source in Methanol to Aromatics

The Preparation of ZSM-5 Zeolite@cu/stainless Steel As a Dual Functional Material

One-step Synthesis of Hierarchical ZSM-5 Zeolites and Their Catalytic Performance on the Conversion of Methanol to Aromatics

A Core-Shell Structured Zn/SiO2@ZSM-5 Catalyst: Preparation and Enhanced Catalytic Properties in Methane Co-Aromatization with Propane

Facile synthesis of hierarchical macro/microporous ZSM-5 zeolite with high catalytic stability in methanol to olefins

Surfactant-assisted hydrothermal synthesis of core-shell ZSM-5@SSZ-13 zeolite for methanol to olefins reaction

Sustainable Synthesis of Core-shell Structured ZSM-5@Silicalite-1 Zeolite

Coating mesoporous ZSM-5 by microporous silicalite-1 shell: Preparation and enhanced catalytic properties in methane co-aromatization with propane

Catalytic Performance of Methanol to Aromatics over Hierarchical ZSM-5 Zeolite Synthesized by a Soft Template Method

Creating Mesopores in ZSM-5 Zeolite by Alkali Treatment: A New Way to Enhance the Catalytic Performance of Methane Dehydroaromatization on Mo/HZSM-5 Catalysts

Catalytic study for methanol aromatization over hierarchical ZSM-5 zeolite synthesized by kaolin

Synthesis of hierarchical ZSM-5 with ultra-small mesopore structure and its catalytic performance during methanol to hydrocarbons

Constructing hierarchical ZSM-5 coated with small ZSM-5 crystals via oriented-attachment and in situ assembly for methanol-to-aromatics reaction

Simultaneously enhanced aromatics selectivity and catalyst lifetime in methanol aromatization over [Zn, Al]-ZSM-5 via isomorphous substitution with optimized acidic properties and pore structure

Core-shell-structured Composite ZSM-5@MCM-41 Catalysts: Fabrication, Characterization, and Enhanced Performance in Hexane Catalytic Cracking

Regulating Hierarchical Structure and Acidity of HZSM-5 for Methanol to Aromatics Via Protective Desiliconization and External Surface Modification

Stable Zn@ZSM-5 catalyst via a dry gel conversion process for methanol-to-aromatics reaction

Methane dehydroaromatization by Mo-supported MFI-type zeolite with core-shell structure

A core-shell structured Zn/ZSM-5@MCM-41 catalyst: Preparation and enhanced catalytic properties in propane aromatization