Abstract:A water-based route has been demonstrated for synthesizing ZnSe and Cd-doped ZnSe (ZnSe(ZnxCd1-xSe, 0 < x < 1) quantum dots (QDs) that have tunable and narrow photo luminescence (PL) peaks from the ultraviolet A (UVA) to the blue range (350-490 nm) with full-width at half-maximum (fwhm) values of 24-36 nm. Hydrazine (N2H4) was used to maintain oxygen-free conditions, allowing the reaction vessel to be open to air. The properties of the QDs were controlled using the thiol ligands, 3-mercaptopropionic acid (MPA), thiolglycolic acid (TGA), and L-glutathione (GSH). On the basis of optical spectra, linear three-carbon MPA attenuated nucleation and growth, yielding small ZnSe QDs with a high density of surface defects. In contrast, TGA and GSH produced larger ZnSe QDs with lower surface defect densities. The absorption spectra show that growth was more uniform and better controlled with linear two-carbon TGA than branched bifunctional GSH. After 20 min of growth TGA-capped ZnSe had an average diameter of 2.5 nm based on high-resolution transmission electron microscopy images; these nanocrystals had an absorbance peak maximum of approximately 340 nm (3.65 eV) and a band gap PL emission peak at 372 nm (3.34 eV). Highly fluorescent ZnxCd1-xSe QDs were fabricated by adding a Cd-thiol complex directly to ZnSe QD solutions; PL peaks were tuned in the blue range (400-490 nm) by changing the Zn to Cd ratio. The Cd-bearing nanocrystals contained proportionally more Se based on X-ray photoelectron spectroscopy, and Cd-Se bonds had ionic character, in contrast to primarily covalent Zn-Se bonds.

Preparation and Characterization of ZnSe Quantum Dots by the Cation-Inverting-injection Method in Aqueous Solution

Synthesis and characterization of ZnSe and ZnSe/ZnS quantum dots for potential biomedical application

Photo-assisted synthesis of highly fluorescent ZnSe(S) quantum dots in aqueous solution

Controlled Synthesis and Characterization of Znse Quantum Dots

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Water-Based Route To Ligand-Selective Synthesis Of Znse And Cd-Doped Znse Quantum Dots With Tunable Ultraviolet A To Blue Photoluminescence

Highly Luminescent and Photostable Core/Shell/Shell ZnSeS/Cu:ZnS/ZnS Quantum Dots Prepared via a Mild Aqueous Route

Optical Control of the Spindle-Liked ZnSe Quantum Dots with Precursor Solvent and Mn Doping

Preparation and Effect of Lighting on Structures and Properties of GSH Capped ZnSe QDs

Phosphine-free Synthesis of High Quality ZnSe, ZnSe/ZnS, and Cu-, Mn-doped ZnSe Nanocrystals.

Kidney transplantation in the dog: surgical technique.

Synthesis And Characterization Of Water-Soluble Cdse/Cds/Zns Core-Shell Quantum Dots

Synthesis of Highly Emissive CdSe Quantum Dots by Aqueous Precipitation Method

Microwave-Assisted Aqueous Synthesis of Transition Metal Ions Doped Znse/Zns Core/Shell Quantum Dots with Tunable White-Light Emission

A Facile Route for Highly Efficient Color-Tunable Cu-Ga-Se/ZnSe Quantum Dots

Preparation of Quantum Dot Light-emitting Diodes Based on the Quantum Dots-CBP Hybrid

Enhanced luminescence of ZnSe:Eu 3+/ZnS core-shell quantum dots

An Aqueous Approach to ZnSe and CdSe Semiconductor Nanocrystals

Synthesis of Highly Emissive Mn-Doped ZnSe Nanocrystals without Pyrophoric Reagents

The synthesis and photocatalytic activity of ZnSe microspheres.

Size- and Shape-Controlled Synthesis of ZnSe Nanocrystals Using SeO2 As Selenium Precursor.