Abstract:A series of manganese-based catalysts supported by 5-10 nm, 10-25 nm, 40 nm and 60 nm anatase TiO2 particles was synthesized via an impregnation method to investigate the effect of the initial support particle size on the selective catalytic reduction (SCR) of NO with NH3. All catalysts were characterized by transmission electron microscopy (TEM), N2 physisorption/desorption, X-ray diffraction (XRD), temperature programmed techniques, X-ray photoelectron spectroscopy (XPS) and in situ diffuse reflectance infrared transform spectroscopy (DRIFTS). TEM results indicated that the particle sizes of the MnO x /TiO2 catalysts were similar after the calcination process, although the initial TiO2 support particle sizes were different. However, the initial TiO2 support particle sizes were found to have a significant influence on the SCR catalytic performance. XPS and NH3-TPD results of the MnO x /TiO2 catalysts illustrated that the surface Mn4+/Mn molar ratio and acid amount could be influenced by the initial TiO2 support particle sizes. The order of surface Mn4+/Mn molar ratio and acid amount over the MnO x /TiO2 catalysts was as follows: MnO x /TiO2(10-25) > MnO x /TiO2(40) > MnO x /TiO2(60) > MnO x /TiO2(5-10), which agreed well with the order of SCR performance. In situ DRIFTS results revealed that the NH3-SCR reactions over MnO x /TiO2 at low temperature occurred via a Langmuir-Hinshelwood mechanism. More importantly, it was found that the bridge and bidentate nitrates were the main active substances for the low-temperature SCR reaction, and bridge nitrate adsorbed on Mn4+ showed superior SCR activity among all the adsorbed NO x species. The variation of the initial TiO2 support particle size over MnO x /TiO2 could change the surface Mn4+/Mn molar ratio, which could influence the adsorption of NO x species, thus bringing about the diversity of the SCR catalytic performance.

Microwave‐Pyrolysis‐Assisted Preparation of Magnetic Iron‐Titanium Mixed Oxide Catalyst for Selective Catalytic Reduction of NOx with NH3

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Magnetic iron-cerium-tungsten mixed oxide pellets prepared through critic acid sol-gel process assisted by microwave irradiation for selective catalytic reduction of NOx with NH3

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Insights over Titanium Modified FeMgOx Catalysts for Selective Catalytic Reduction of NOx with NH3: Influence of Precursors and Crystalline Structures

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Transition metals (Co, Zr, Ti) modified iron-samarium oxide as efficient catalysts for selective catalytic reduction of NOx at low-temperature

Promotional effect of tungsten modification on magnetic iron oxide catalyst for selective catalytic reduction of NO with NH3

Novel Mn-Ce-Ti Mixed-Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH₃.

Promoting Effect of Ti Species in MnOx-FeOx/Silicalite-1 for the Low-Temperature NH3-SCR Reaction

Mechanism and Kinetics Study on Low-Temperature NH3-SCR over Manganese–Cerium Composite Oxide Catalysts

A Novel MnOx–MoOx Codoped Iron-Based Catalyst for NH3-SCR with Superior Catalytic Activity over a Wide Temperature Range

Effect of Preferential Exposure of Anatase TiO2 {0 0 1} Facets on the Performance of Mn-Ce/TiO2 Catalysts for Low-Temperature Selective Catalytic Reduction of NOx with NH3

Promotional effect of iron oxide on the catalytic properties of Fe–MnOx/TiO2 (anatase) catalysts for the SCR reaction at low temperatures

Activity and Characterization of Ce–Mo–Ti Mixed Oxide Catalysts Prepared by a Homogeneous Precipitation Method for Selective Catalytic Reduction of NO with NH3

Selective catalytic reduction of NOx with NH3 over iron-cerium-tungsten mixed oxide catalyst prepared by different methods

Preparation of Cr-Mn Mixed Oxide by Coprecipitation and Its Performance for Low-Temperature Selective Catalytic Reduction of NOx

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Effect of Initial Support Particle Size of MnOx/TiO2 Catalysts in the Selective Catalytic Reduction of NO with NH3

Low-Temperature Selective Catalytic Reduction of NOx with NH3 over Fe–Mn Mixed-Oxide Catalysts Containing Fe3Mn3O8 Phase

Effect of Metal Complexing on Mn–Fe/TS-1 Catalysts for Selective Catalytic Reduction of NO with NH3