Thermal Stability and Hardening Behavior in Superelastic Ni-rich Nitinol Alloys with Al Addition

H. Chen,L. J. Zheng,F. X. Zhang,H. Zhang

DOI: https://doi.org/10.1016/j.msea.2017.10.016

2017-01-01

Abstract:Ni-rich NiTi alloys exhibit high hardness of 58–65HRC, comparable to tool steels. Ni-rich NiTi alloys combine hard, corrosion resistant, nonmagnetic and other attributes that makes them promising candidates for bearing and related applications. The high hardness has been associated with the precipitation of a large volume fraction of nano-sized Ni4Ti3 strengthening phase. In this work, a series of Ni55Ti45−xAlx (x = 4, 6, 8at%) ternary alloys have been prepared to explore the microstructural evolution, hardening behavior and thermal stability in Ni-rich NiTi alloys with Al additions. For comparison purposes, the binary 55Ni-45Ti alloy was also examined. TEM results revealed that the Al additions refined the Ni4Ti3 phase to a few nanometers, as a result, the ternary alloys showed higher hardness than binary alloy. After aging for 96h at 500°C, the hardness of ternary alloy (55Ni-39Ti-6Al) remained above 820 HV, significantly superior to binary alloy was lower than 700HV. Upon aging at 600°C for 96h, the hardness of 55Ni-39Ti-6Al could reach over 700HV, while the binary alloy's hardness decreased dramatically to about 400HV. It was because there were still nano-sized Ni4Ti3 precipitates in ternary alloys while the Ni4Ti3 phase in binary 55Ni-45Ti alloy had completely decomposed. Thus, the Al additions increased the hardness of Ni-rich NiTi alloys by refining the strengthening phase Ni4Ti3 and improve the thermal stability of Ni4Ti3 phase. The study results enhance the hardness of Ni-rich NiTi alloys and raise the working temperature. Therefore, it would make contributions to the development of new generation NiTi based bearing alloy.