Abstract:In the present paper, cracking sequence of high-strength engineered cementitious composite with the characteristic of low drying shrinkage (LSECC) under tension was experimentally studied by continually photographing during loading. The specific objective is to investigate the development of crack opening of each individual crack occurred during loading. Four Engineered cementations composite mixtures with water to binder ratio of 0.20, 0.25, 0.30, and 0.35 (LSECC-0.20, LSECC-0.25, LSECC-0.30, and LSECC-0.35) were used in the tests. Using the photographers taken during the test, crack width of each crack occurred during loading are determined according to the difference between solid material and crack on gray level. The test results show that cracks in ECC under tensile load are formed according to a temporal sequence. The opening width of each crack grows in a controllable and gradual manner with the increase of tensile strain. At a given strain level, crack width of different crack is not equal and the distribution of crack width is affected by matrix strength of the composite. Maximum crack width and the tensile strain capacity at the moment may be utilized to characterize the tensile performance of the composite that can guarantee both of tensile ductility and long-term durability. As maximum crack width equals 60 μm, at which the permeability of ECC may not be influenced by the cracks, higher strength ECC with water to binder ratio of 0.20 and 0.25 (LSECC-0.20 and LSECC-0.25) shows obvious higher tensile strain capacity and more cracks of narrow opening. By contrast, lower strength ECC with water to binder ratio of 0.30 and 0.35 (LSECC-0.30 and LSECC-0.35) shows relatively lower tensile strain and fewer cracks of narrow crack opening as crack width is limited below 60 μm. With the increase of tensile strain and the maximum crack width, much wider cracks (larger than 60 μm) are formed in lower strength ECC comparing to that of higher strength ECC.

Using Eccentrically Sample to Find the Relationship Between Resistivity and Cracking Time in Cement Paste Vides Mechanical Strength and Electrical Resistivity

Critical Features of Microstructure Development of Early-Age Cement Paste Revealed by Non-Contact Electrical Resistivity Measurement

A Mathematical Model for the Electrical Resistivity of Cement Paste at Early Ages Considering the Partially Saturated State

A Study on the Relationship Between the Performance of External Thermal Insulating Anti-Crack Mortar and Maintenance Time

Correlation of Mechanical and Microstructure Development of Early-Age Concrete by Electrical Resistivity Measurement

Early Age Properties and Cracking Control of Concrete

Simple Three-Step Analytical Scheme for Prediction of Elastic Moduli of Hardened Cement Paste

Influence of Recycled Cement Paste Powder on Early-Age Plastic Shrinkage and Cracking of Cement-Based Materials

Monitoring the hydration behavior of hardened cement paste affected by different environmental pH regimes

Fracture Toughness And Microstructure Of Concrete At Early-Ages

THEORETICAL INVESTIGATION TO CRACKING PREDICTION OF EARLY-AGE CONCRETE

Mechanical and Microstructure Characterization of Fresh High- and Normal- Strength Concrete with Non-Contact Electrical Resistivity Measurement

Modeling of Time to Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Interpretation of Microstructure Development of Early-Age Concrete by Electrical Resistivity Measurement

Unveil the Role of Nano-Caco3 in Early Shrinkage and Tensile Properties of Cement Paste: from Experimental Work to Modeling

Modeling on mechanical properties of concrete based on cement hydration degree

Electrical Resistivity of Cement Pastes Undergoing Cyclic Freeze-Thaw Action

Prediction of micro creep behavior of hardened cement paste based on the isotache model of clays

Comparative analysis of very-early age hydration process: LC3 vs. conventional and blended cement pastes using embedded piezo sensors

Strain-rate Sensitivity of Cement Paste by Microindentation Continuous Stiffness Measurement: Implication to Isotache Approach for Creep Modeling

Mapping of cracking sequence of polyvinyl alcohol-steel hybrid fiber reinforced high-strength engineered cementitious composite under uniaxial tension