Eutectic Formation During Solidification of Ni-Based Single-Crystal Superalloys with Additional Carbon

Fu Wang,Dexin Ma,Andreas Bührig-Polaczek

DOI: https://doi.org/10.1007/s11661-017-4317-1

2017-01-01

Abstract:γ/γ′ eutectics’ nucleation behavior during the solidification of a single-crystal superalloy with additional carbon was investigated by using directional solidification quenching method. The results show that the nucleation of the γ/γ′ eutectics can directly occur on the existing γ dendrites, directly in the remaining liquid, or on the primary MC-type carbides. The γ/γ′ eutectics formed through the latter two mechanisms have different crystal orientations than that of the γ matrix. This suggests that the conventional Ni-based single-crystal superalloy castings with additional carbon only guarantee the monocrystallinity of the γ matrix and some γ/γ′ eutectics and, in addition to the carbides, there are other misoriented polycrystalline microstructures existing in macroscopically considered “single-crystal” superalloy castings.