Abstract:In ceramic/metal brazing, high residual stress usually causes fracture in the ceramic substrates. Therefore, composite fillers consisting of ductile matrix featuring low yield strength and elastic modulus, as well as reinforcements featuring low coefficient of thermal expansion (CTE), are employed. However, for AgCuTi-base composite fillers, the reinforcements are likely to weaken the deformability of brazing seams (BS), i.e. increase the elastic modulus and yield stress of BS. To address this issue, we developed a new AgCu-base composite filler with "hedgehog-like" reinforcement clusters. Herein, AgCu + NbB2 composite filler was used to braze ZrB2-SiC and TC4-TiBw, wherein ductile Ag(s,s) and Cu(s,s) dominated BS, thereby ensuring high deformability; in addition, a NbB layer along with limited TiB whiskers was formed at the NbB2/brazes interface with the orientation relationship of (-11-1)NbB//(0-1-1)TiB and [-314]NbB//[12-2]TiB, resulting in "hedgehog-like" reinforcement clusters. This structure exhibited the following advantages: (i) crystallographic misfit at the interface of reinforcement clusters/brazes and the controlled formation of TiB whiskers minimised the conventional fine grain strengthening and dispersion strengthening effects of BS; (ii) isolated reinforcement clusters decelerated the increase in the elastic property of BS; (iii) "hedgehog-like" structure absorbed fracture energy by deflecting cracks; and (iv) the formation of brittle compounds could be avoided. In other words, the designed reinforcement clusters reduced the deformability expense and compensated for the mechanical-resistance of BS. Therefore, the maximum joint strength was obtained with 2 wt% NbB2, which increased the shear strength of the joint six times compared to that with 0 wt% NbB2. For the joints failing inside ceramic substrates, (i) the key factor for limiting joint strength was the residual stress inside ceramics and (ii) the remission of the trade-off between thermal expansion mismatch and deformability expense contributed to relaxing residual stress, thereby confirming the reliability of our design.

Brazing ZrO2 Ceramic and TC4 Alloy by Novel WB Reinforced Ag-Cu Composite Filler: Microstructure and Properties

Interfacial Reaction Behavior and Mechanical Characterization of ZrO2/TC4 Joint Brazed by Ag–Cu Filler Metal

Interfacial Microstructure and Properties of TZM Alloy and ZrCp-W Composite Joints Brazed Using Ti-50Ni Filler

Brazing SiC Ceramic Using Novel B4C Reinforced Ag–Cu–Ti Composite Filler

Brazing of TiBw/TC4 Composite and Ti60 Alloy Using TiZrNiCu Amorphous Filler Alloy

Characterization of ZTA Composite Ceramic/Ti6Al4V Alloy Joints Brazed by AgCu Filler Alloy Reinforced with One-Dimensional Al<sub>18</sub>B<sub>4</sub>O<sub>33</sub> Single Crystal

Vacuum Brazing ZSCf Composite Ceramics to TC4 Alloy with Ag-Cu Filler

Interfacial Microstructure and Mechanical Properties of TZM Alloy and ZrC Particle Reinforced Tungsten Composite Joint Brazed Using Ti-61Ni Filler

Brazing of TC4 Alloy Using Ti-Zr-Ni-Cu-Sn Amorphous Braze Fillers

Solid-state Transformation Composite Filler: A New Strategy to Strengthen Ceramic/metal Joint

Improvement for Ti3SiC2/Cu Joint Brazed Using Composite Fillers with Abnormal Expansion Ceramic Particulates

Microstructure and Mechanical Properties of ZrB2–SiC Ultrahigh Temperature Ceramic Composite Joint Using TiZrNiCu Filler Metal

Interfacial Microstructure and Mechanical Properties of ZrB2SiC C Ceramic and GH99 Superalloy Joints Brazed with a Ti-modified FeCoNiCrCu High-Entropy Alloy

Design of composite filler with hedgehog-like reinforcement clusters for effective stress relief in ceramic/metal joints

Brazing of ZrB 2 –SiC–C ceramic and GH99 superalloy to form reticular seam with low residual stress

Active Brazing Carbon/carbon Composite to TC4 with Cu and Mo Composite Interlayers

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

Brazing ZTA Ceramic to TC4 Alloy Using the Cu Foam As Interlayer

Investigating the Effect of WC Reinforcements in Cu Ti Composite Filler on the Microstructural Evolution and Mechanical Characteristics in Brazing Cf/SiC and GH3536

Investigating the effect of WC reinforcements in Cu Ti composite filler on the microstructural evolution and mechanical characteristics in brazing C f /SiC and GH3536

Microstructure and Mechanical Properties of Al2O3/Cu Joints Brazed with Ag–Cu–Ti+Zn Composite Fillers