Abstract:In ceramic/metal brazing, high residual stress usually causes fracture in the ceramic substrates. Therefore, composite fillers consisting of ductile matrix featuring low yield strength and elastic modulus, as well as reinforcements featuring low coefficient of thermal expansion (CTE), are employed. However, for AgCuTi-base composite fillers, the reinforcements are likely to weaken the deformability of brazing seams (BS), i.e. increase the elastic modulus and yield stress of BS. To address this issue, we developed a new AgCu-base composite filler with "hedgehog-like" reinforcement clusters. Herein, AgCu + NbB2 composite filler was used to braze ZrB2-SiC and TC4-TiBw, wherein ductile Ag(s,s) and Cu(s,s) dominated BS, thereby ensuring high deformability; in addition, a NbB layer along with limited TiB whiskers was formed at the NbB2/brazes interface with the orientation relationship of (-11-1)NbB//(0-1-1)TiB and [-314]NbB//[12-2]TiB, resulting in "hedgehog-like" reinforcement clusters. This structure exhibited the following advantages: (i) crystallographic misfit at the interface of reinforcement clusters/brazes and the controlled formation of TiB whiskers minimised the conventional fine grain strengthening and dispersion strengthening effects of BS; (ii) isolated reinforcement clusters decelerated the increase in the elastic property of BS; (iii) "hedgehog-like" structure absorbed fracture energy by deflecting cracks; and (iv) the formation of brittle compounds could be avoided. In other words, the designed reinforcement clusters reduced the deformability expense and compensated for the mechanical-resistance of BS. Therefore, the maximum joint strength was obtained with 2 wt% NbB2, which increased the shear strength of the joint six times compared to that with 0 wt% NbB2. For the joints failing inside ceramic substrates, (i) the key factor for limiting joint strength was the residual stress inside ceramics and (ii) the remission of the trade-off between thermal expansion mismatch and deformability expense contributed to relaxing residual stress, thereby confirming the reliability of our design.

Solid-state Transformation Composite Filler: A New Strategy to Strengthen Ceramic/metal Joint

Unveiling Solid-State Transformation Toughening Mechanism of Yttria Stabilized Zirconia on Brazed Joint by In-Situ Observation

Improvement for Ti3SiC2/Cu Joint Brazed Using Composite Fillers with Abnormal Expansion Ceramic Particulates

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

Brazing ZrO2 Ceramic and TC4 Alloy by Novel WB Reinforced Ag-Cu Composite Filler: Microstructure and Properties

Design of composite filler with hedgehog-like reinforcement clusters for effective stress relief in ceramic/metal joints

Design of Multi-Layered Architecture in Dissimilar Ceramic/metal Joints with Reinforcements Clustering Away from Both Substrates

Pressureless brazing of zirconia to stainless steel using active filler metal with TiH2 powder

Reactive air brazing of YSZ ceramic with novel Al2O3 nanoparticles reinforced Ag-CuO-Al2O3 composite filler: Microstructure and joint properties

Brazing SiO2f/SiO2 Composite to Invar Alloy Using a Novel TiO2 Particle-Modified Composite Braze Filler

Brazing SiC Ceramic Using Novel B4C Reinforced Ag–Cu–Ti Composite Filler

Interfacial microstructure and mechanical properties of joints between ZrO 2 ceramic and 316 stainless steel brazed using Ag–Cu–In–Ti filler

Joining of Yttria Stabilised Zirconia to Ti6Al4V Alloy Using Novel CuO Nanostructure Reinforced Cu Foam Interlayer

Effect of AgCu/Cu Foam/agcu Composite Filler on Microstructure and Mechanical Properties of ZrB2-SiC/Inconel 600 Alloy Brazed Joints

Microstructure and strength of zirconia/stainless steel joints prepared by pressureless active brazing

Brazing YSZ ceramics by a novel SiO2 nanoparticles modified Ag filler

Microstructures and Interfacial Behavior of Zirconia/stainless Steel Joint Prepared by Pressureless Active Brazing

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal

Joining of SiO2 Ceramic and TC4 Alloy by Nanoparticles Modified Brazing Filler Metal

Microstructure and Mechanical Properties of the SiC/Nb Joint Brazed Using AgCuTi + B4C Composite Filler Metal

Interfacial Microstructure and Mechanical Properties of Ultrasonic-Assisted Brazing Joints Between Ti–6Al–4V and ZrO2