Abstract:Due to moisture in the ore, auxiliary material, and ladle refractory material, the hydrogen element is easily enriched in molten steel. In the metallurgy process, some hydrogen atoms form bubbles and are removed by gravity, whearas others solidify in the strand and remain in the produced steel. When the hydrogen content reaches a certain critical value, the enriched hydrogen atoms congregate to produce a white spot, which greatly reduces the strength and toughness of the steel product, and leads to brittle fracture during its service period. At present, the RH (Ruhrstahl–Heraeus) and VD (vacuum degasser) refining processes are commonly applied in steel plants, which can reduce the hydrogen content to less than 2×10−6. With the demand for high quality steel, the hydrogen content must be further decreased, so hydrogen diffusion in solid steel during the annealing process is gradually attracting increasing attention. In this study, a two-dimensional model was built to investigate the characteristic of dehydrogenation in the bloom annealing process of rail steel. Moreover, the effect of annealing temperature and annealing time on hydrogen diffusion were analyzed, and the annealing parameters were optimized. During the dehydrogenation annealing process, the hydrogen content at the corners and edges of the bloom are found to decrease rapidly, while that in the center of the strand begin to decrease in the later heating stage. As the annealing temperature increases, the starting point of dehydrogenation in the bloom center moves ahead and the maximum dehydrogenation rate increases significantly. With the extension of the soaking period, the central hydrogen content of bloom decreases significantly, but the increase rate of the dehydrogenation gradually decreases. By optimizing the bloom annealing parameters, the hydrogen content in the bloom can be steadily reduced to 0.6×10−6, which fully meets the requirement of high quality steel production.

Study and Application of a Simplified Soft Reduction Amount Model for Improved Internal Quality of Continuous Casting Bloom

Simulation Analysis of Thermal Stress During Casting Process of Large-Sized Alloy Steel Ingot

Analysis of Internal Cracks in High Carbon Casting Bloom Induced by Soft Reduction Process and Its Improvement Using Numerical Simulations and Industrial Experiments

Alleviation Of Internal Cracks In Continuous Casting Bloom Of Steel 100cr6 Induced By Soft Reduction Process

Modeling and Control of Dynamic Soft Reduction in Continuous Slab Casting

Controlling Centre Segregation and Shrinkage Cavities Without Internal Crack in As-Cast Bloom of Steel GCr15 Induced by Soft Reduction Technologies

Numerical Simulation of Dehydrogenation Annealing in Bloom

Homogenization Path Based on 250 mm × 280 mm Bloom under Mixed Light and Heavy Presses: Simulation and Industrial Studies

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

Comparative Studies on a Chamfer Technology and a Convex Roll Technology During the Soft Reduction Process

High-efficiency continuous casting of GCr15 bearing steel bloom based on cooperative control technique of complex electromagnetic stirring and soft reduction

Numerical simulation on the centre macrosegregation during Billet continuous casting with the soft reduction

Application Situation of Soft Reduction During Process of Slab Continuous Casting

Modelling of continuous casting processes parameters on the shrinkage cavity formation in bearing steel blooms

SIMULATION STUDY ON SOFT REDUCTION ZONE FOR CONTINUOUSLY CAST PIPELINE STEEL

Propagation form of internal cracks induced by continuous casting soft reduction and control strategy for internal quality

Influence of Differential Reduction Rate in Adjacent Roll Reduction Zone on Internal Cracks of High Carbon Bloom Induced by Mechanical Soft Reduction

INFLUENCE OF INTERNAL CRACKING ON CARBIDE PRECIPITATION IN CONTINUOUS CASTING BLOOM INDUCED BY SOFT REDUCTION TECHNOLOGY AND THE RESULTING SEGREGATED BAND IN HOT-ROLLED WIRE RODS

Influence of mechanical reduction amount on internal quality of continuous casting billets by thermal and numerical simulation

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Analysis and Control of Central Cracks in the Bloom Continuous Casting of Microalloy 49mnvs3 Steel