Abstract:The centerline segregation in continuous casting steel is known to be formed by the interdendritic enriched liquid flow at the solidification end in strand.At present,several methods,such as thermal soft reduction, electromagnetic stirring and dynamic soft reduction,are available to reduce the center segregation and to improve the internal quality.Although some methods could alleviate center segregation to some extent,they can also give rise to new problems.For instance,thermal soft reduction can lead to surface cracking during casting of some steels and electromagnetic stirring can result in white band.Dynamic soft reduction is an effective technology for the improvement of strand quality in continuous slab casting.In this paper,the key parameters of dynamic soft reduction technology,such as soft reduction region,the total reduction amount,for low carbon steel have been studied based on experimental and theoretical analysis.The soft reduction region was related to the segregation of chemical composition,slab bulging of narrow side and avoiding internal crack of slab.The total reduction amount was composed of natural thermal shrinkage and actual reduction amount depending on critical strain.For low carbon steel with slab dimension of(950 - 1 950) mm×170 mm,the solid fraction range in soft reduction region was recommended from 0.4 to 0.8,the total reduction amount was 2.0 -2.8 mm,and the optimized reduction rate was 0.4 - 1.2 mm/min,respectively.Furthermore,a dynamic soft reduction system in continuous slab casting, Visual Cast-Dynamic,has been developed by multithreading method.It demonstrated that the dynamic soft reduction model in this study was correct with the ability of online control.

Alleviation Of Internal Cracks In Continuous Casting Bloom Of Steel 100cr6 Induced By Soft Reduction Process

Analysis of Internal Cracks in High Carbon Casting Bloom Induced by Soft Reduction Process and Its Improvement Using Numerical Simulations and Industrial Experiments

Controlling Centre Segregation and Shrinkage Cavities Without Internal Crack in As-Cast Bloom of Steel GCr15 Induced by Soft Reduction Technologies

Simulation Analysis of Thermal Stress During Casting Process of Large-Sized Alloy Steel Ingot

Propagation form of internal cracks induced by continuous casting soft reduction and control strategy for internal quality

Influence of Differential Reduction Rate in Adjacent Roll Reduction Zone on Internal Cracks of High Carbon Bloom Induced by Mechanical Soft Reduction

Analysis of Internal Cracks in Continuous Casting Slabs with Soft Reduction

INFLUENCE OF INTERNAL CRACKING ON CARBIDE PRECIPITATION IN CONTINUOUS CASTING BLOOM INDUCED BY SOFT REDUCTION TECHNOLOGY AND THE RESULTING SEGREGATED BAND IN HOT-ROLLED WIRE RODS

Modeling and Control of Dynamic Soft Reduction in Continuous Slab Casting

Continuous Casting Mould for Square Steel Billet Optimised by Solidification Shrinkage Simulation

Analysis and Control of Central Cracks in the Bloom Continuous Casting of Microalloy 49mnvs3 Steel

Effect of soft reduction process on segregation of a 400 mm thick high-alloy steel slab

Application Situation of Soft Reduction During Process of Slab Continuous Casting

Comparative Studies on a Chamfer Technology and a Convex Roll Technology During the Soft Reduction Process

Numerical Modelling of Chamfer Billet of High Carbon Steel During Continuous Casting

Optimization for Secondary Cooling Parameters in Continuous Casting of High Carbon Chromium Bearing Steel

Analysis and control of surface cracks in a B-bearing continuous casting blooms

Analysis of Longitudinal Cracking and Mold Flux Optimization in High-Speed Continuous Casting of Hyper-Peritectic Steel Thin Slabs

Improving Inner Quality in Continuous Casting Rectangular Billets: Comparison Between Mechanical Soft Reduction and Final Electromagnetic Stirring

Homogenization Path Based on 250 mm × 280 mm Bloom under Mixed Light and Heavy Presses: Simulation and Industrial Studies

Numerical simulation on the centre macrosegregation during Billet continuous casting with the soft reduction