Abstract:Finite element analyses of oxygen diffusion at the grain level have been carried out for a polycrystalline nickel-based superalloy, aiming to quantify the oxidation damage under surface oxidation conditions at high temperature. Grain microstructures were considered explicitly in the finite element model where the grain boundary was taken as the primary path for oxygen diffusion. The model has been used to simulate natural diffusion of oxygen at temperatures between 650∘C and 800∘C, which are controlled by the parabolic oxidation rate and oxygen diffusivity. To study the effects of mechanical stress on oxygen diffusion, a sequentially coupled deformation-diffusion analysis was carried out for a generic specimen geometry under creep loading condition using a submodeling technique. The material constitutive behavior was described by a crystal plasticity model at the grain level and a unified viscoplasticity model at the global level, respectively. The stress-assisted oxygen diffusion was driven by the gradient of hydrostatic stress in terms of pressure factor. Heterogeneous deformation presented at the grain level imposes a great influence on oxygen diffusion at 750∘C and above, leading to further penetration of oxygen into the bulk material. Increased load level and temperature enhance oxygen concentration and penetration within the material. At 700∘C and below, mechanical loading seems to have negligible influence on the oxygen penetration because of the extremely low values of oxygen diffusivity and pressure factor. In the case of an existing surface microcrack, oxygen tends to accumulate around the crack tip due to the high stress level presented near the crack tip, leading to localized material embrittlement and promotion of rapid crack propagation.

Modification of the Mechanism for Stress-Aided Grain Boundary Oxidation Ahead of Cracks

Defect-driven Selective Metal Oxidation at Atomic Scale.

A diffusion-based approach for modelling crack tip behaviour under fatigue-oxidation conditions

Modeling of Oxygen Diffusion Along Grain Boundaries in a Nickel-Based Superalloy

Oxidation at High Temperature under Three-Point Bending Considering Stress-Diffusion Coupling Effects

Diffusive crack-grain interplay in freestanding nanocrystalline silver thin film

Diffusion and Stress Coupling Effect During Oxidation at High Temperature

Oxidation-induced recrystallization and damage mechanism of a Ni-based single-crystal superalloy during creep

On the role of plastic relaxation in stress assisted grain boundary oxidation

Effect of oxidation on crack propagation of Si nanofilm: A ReaxFF molecular dynamics simulation study

Chemo-mechanical Coupling Effect on Bidirectional Diffusion Process During Oxidation

A Dominant Role of Stress-Dependent Oxide Structure on Diffusion Flux in the Strain-Reaction Engineering

Insight into the acceleration in oxidation kinetics ahead of stress corrosion crack of alloy 690 in simulated PWR primary water

Self-Induced Internal Corrosion Stress Transgranular Cracking in Gradient-Structural Ploycrystalline Materials at High Temperature

Computational Modelling of Crack Initiation in a Single Crystal Superalloy under Fatigue–oxidation Conditions

Oxidation Stress Evolution and Relaxation of Oxide Film/Metal Substrate System

A finite element simulation on fully coupled diffusion, stress and chemical reaction

Interplay between fracture and diffusion behaviors: Modeling and phase field computation

A Multiscale Approach for Coupled Phenomena in Fcc Materials at High Temperatures

Atomistic Scale Behaviors of Intergranular Crack Propagation along Twist Grain Boundary in Iron under Dynamic Loading

Stresses from Oxide Film Imperfections During Metal Dusting