Abstract:This study investigates the long-term performance of laboratory dam concrete in different curing environments over ten years and the microstructure of 17-year-old laboratory concrete and actual concrete cores drilled from the Three Gorges Dam. The mechanical properties of the laboratory dam concrete, whether cured in natural or standard environments, continued to improve over time. Furthermore, the laboratory dam concrete exhibited good resistance to diffusion and a refined microstructure after 17 years. However, curing and long-term exposure to the local natural environment reduced the frost resistance. Microstructural analyses of the laboratory concrete samples demonstrated that moderate-heat cement and fine fly ash (FA) particles were almost fully hydrated to form compact microstructures consisting of large quantities of homogeneous C-(A)-S-H gels and a few crystals. No obvious interfacial transition zones were observed in the microstructure owing to the long-term pozzolanic reaction. This dense and homogenous microstructure was the crucial reason for the excellent long-term performance of the dam concrete. A high FA volume also played a significant role in the microstructural densification and performance growth of dam concrete at a later age. The concrete drilled from the dam surface exhibited a loose microstructure with higher microporosity, indicating that concrete directly exposed to the actual service environment suffered degradation caused by water and wind attacks. In this study, both macro performance and microstructural analyses revealed that the application of moderate-heat cement and FA resulted in a dense and homogenous microstructure, which ensured the excellent long-term performance of concrete from the Three Gorges Dam after 17 years. Long-term exposure to an actual service environment may lead to microstructural degradation of the concrete surface. Therefore, the retained long-term dam concrete samples need to be further researched to better understand its microstructural evolution and development of its properties.

Simulation of Mechanical Properties of Light-Burned Magnesium Oxide-Containing Concrete for Historical Dam Temperatures

Effect of Curing Conditions on Property of High Performance Concrete with Composite Mineral Admixture

Effect of Working Temperature Conditions on the Autogenous Deformation of High-Performance Concrete Mixed with MgO Expansive Agent

A Mathematical Model of the Expansion Evolution of Magnesium Oxide in Mass Concrete Based on Hydration Characteristics

Modeling and Mesoscale Simulation of Ice-Strengthened Mechanical Properties of Concrete at Low Temperatures

Hydration and durability of low-heat cementitious composites for dam concrete: Thermodynamic modeling and experiments

Analysis of Expansion Effect of Magnesium Oxide(mgo) in Mass Concrete

Experimental Study of Mechanical Properties of Normal-Strength Concrete Exposed to High Temperatures at an Early Age

Damage and deterioration characteristics of basic magnesium sulfate cement-coral aggregate concrete exposed to elevated temperature

Long-Term Performance and Microstructural Characterization of Dam Concrete in the Three Gorges Project

Influence of Steam Curing Method on the Performance of Concrete Containing a Large Portion of Mineral Admixtures

Cementitious and hardening properties of magnesia (MgO) under ambient curing conditions

Evaluation of Mechanical Properties of Concrete after Exposure to Elevated Temperatures Using Ultrasonic Pulse Velocity Measurement and a Split-Hopkinson Pressure Bar

Mechanical properties, pore characteristics and microstructure of modified magnesium slag cemented coal-based solid waste backfill materials: Affected by fly ash addition and curing temperature

Experimental research on properties of magnesium oxysulfate cement during high temperature exposure

Evaluation of Early Age Mechanical Properties of Concrete in Real Structure

Experimental Study on Mechanical Properties of Early-Aged Concrete after Exposure to High Temperatures

Experimental Investigation of the Static Expansion Tensile Behavior of Concrete after Exposure to Elevated Temperatures

Comparison Between Mechanical Properties of Dam and Sieved Concretes

Effect of Curing Temperature on Mechanical Strength and Thermal Properties of Hydraulic Limestone Powder Concrete

Mechanical properties of concrete at high temperature—A review