A Study on the Kinetics of Leaching the Residues from the Neutral Leaching Process with High Concentration of Sulfuric Acid at High Temperature
Zhi-hua XIA,Mo-tang TANG,Shi-qing LI,Yan LUO,Chao-bo TANG
DOI: https://doi.org/10.3969/j.issn.0253-6099.2005.02.017
2005-01-01
Abstract:The kinetics of leaching the residues from the neutral leaching process with high concentration of sulphuric acid at high temperature was investigated .The effects of reaction temperature, concentration of reagents, the size of residue granule, agitation rate and concentration of metal ions on the leaching process were studied. The results show that the leaching process can be simulated with a shrinking core model. Because the residue contains not only zinc ferrite, but also zinc oxide and other zinc species, the leaching process is composed of three stages distinguished by the leaching time. During the first stage (≤15 min),leaching is very fast for solving ZnSO 4(s) and part of ZnO(the zinc leaching fraction is higher than 0.35). During the second stage (15～60 min), zinc oxide and other zinc species are soluted chiefly. The activation energy was determined to be about 51.792 kJ/mol, and the leaching rate is controlled by the surface chemical reaction. The reaction progressions of H +,Zn 2+ and Fe 3+ are 1.0771,-1.764 and -1.391,respectively. While in the third stage (60～300 min), zinc ferrite and zinc sulfate were mainly leached out slowly. The activation energy was determined to be about 20.72 kJ/mol, The leaching rate is controlled by the mixed surface chemical reaction and outside diffusion, the reaction progressions of H +,Zn 2+ and Fe 3+ are 0.3993, -0.3767,and -0.4456, respectively.