Abstract:Superacid catalyst SO42--ZrO2/TiO2 was applied in esterification of Acetic Acid and Butanol. The particle size of ZrO2 in the catalyst was about 12.5 nm. In catalyst preparation conditions, the effect factor order on catalytic activity is H2SO4 concentration ＞ calcination temperature ＞ ZrO2 supported content. The optimum preparation condition is as follows: ZrO2 content 3.5g/g; calcination temperature 600℃, and H2SO4 concentration 0.5mol/L. The catalytic activity is 96.5 vol%.SO42-/MxOy solid superacid is a kind of green catalyst, whose application perspective is bright. In this paper, SO42--ZrO2/TiO2 solid superacid was prepared with nanometer compound carrying method. The acidic strength of catalysts was measured with the following Hammett indicators, 2,4-dinitrofluorobenzene (H0=-14.52) and p-nitrochlorobenzene (H0=-12.70). Catalytic activity was evaluated with esterification reaction of Acetic Acid and Butanol. Reaction temperature was at 105℃, and reaction time was only 1h. The conversion rate of Acetic Acid was analyzed by a gas chromatograph (GC-14C SHIMADZU in Japan)The experimental results showed that H2SO4 concentration had more influences on catalytic activity than other two factors, calcination temperature and ZrO2 supported content. Since sulfur absorbed on the surface of metal oxides is necessary to the acidity of SO42-/MxOy solid superacid,H2SO4 concentration in impregnation solution is needed enough high. But, it can't be too much high,otherwise, Zirconium sulfate formed on the catalyst surface will be harmful influences on catalytic activity. In researched cover, 0.5mol/L H2SO4 concentration is the most suitable, and the catalyst prepared with this concentration has very strong acidity.The optimum preparation condition is as follows: ZrO2 content 3.5g/g; calcination temperature 600℃, and H2SO4 concentration 0.5mol/L. In the catalyst prepared with above conditions, the acidic strength (H0) of the catalyst is smaller than ＜-14.52, and catalytic activity is 96.5 vol%. When it was re-used

Studies on Preparation and Catalytic Performances of Monolithic Solid Acid Catalysts

Preparation of Fibrous SO42-/ZrO2-Nio Solid Acid Catalyst, Characterization and its Catalytic Properties

Studies on n-butane isomerization reaction on solid oxide super acid Pt-SO4 2- /ZrO2-Al2O3 catalysts

Preparation of Fibrous SO<sub>4</sub><sup>2-</sup>/ZrO<sub>2</sub>-Nio Solid Acid Catalyst, Characterization and Its Catalytic Properties

A Facile Route for Spraying Preparation of Pt/TiO2 Monolithic Catalysts Toward VOCs Combustion

Preparation and characterization of Zr(SO4)2/TiO2 catalyst

Catalysis of SO42--ZrO2/TiO2 Nanometer Solid Superacid

Enhancement of SCR Activity and Mechanical Stability on Cordierite Supported V2O5-WO3/TiO2 Catalyst by Substrate Acid Pretreatment and Addition of Silica

Preparation and Catalytic Performance of SO2-4/ZrO2-SiO2 Solid Superacid

Mass Transfer Enhancement and Drying Mechanism of High Adhesion Saturated Impregnated Co-Al2O3 Monolithic Catalyst

Preparation of Cordierite-supported Solid Acid Catalyst for Esterification

Preparation and properties of ultrafine SO4 2- /ZrO2 superacid catalysts

Studies on γ-Al2O3 Supported Cr Promoted SO2- 4/ZrO2 Solid Superacid Catalysts

Studies on Gamma-Al2o3 Supported Cr Promoted So42-/Zro2 Solid Superacid Catalysts

Preparation and Characterization of SO;/TiO; and S;O;/TiO; Catalysts

A New Way to Prepare Some Supported Catalysts with Highly Specific Surfaces

Preparation and Properties of Ultrafine SO42−/ZrO2 Superacid Catalysts

Preparation and Catalytic Properties of Composite Titanium-Zirconium Oxides

Preparation and characterization of Cu(I)/SO42-/ZnO and Cu(I)/S2O82-/ZnO catalysts

Construction of Ti-containing zeolite with highly enhanced catalytic activity by active species surface implanting strategy

Enhanced Esterification Performance of Layered SO42−/TiO2‐H3Ti5NbO14 Solid Acid Catalyst