Effects of hydrogen partial pressure on crack initiation and growth rate in vintage X52 steel
Fernando D. León-Cázares,Milan Agnani,Joseph Ronevich,Chris San Marchi
DOI: https://doi.org/10.1016/j.ijhydene.2024.02.292
IF: 7.2
2024-02-01
International Journal of Hydrogen Energy
Abstract:There is an increasing interest in ensuring compatibility of existing natural gas infrastructure with conveyance of hydrogen, especially for vintage (pre-1970s) pipeline steels. While hydrogen is known to affect the fatigue and fracture resistance of these materials, there is a lack of data on its effects on crack initiation at low hydrogen partial pressure. To address this gap, the current work presents a series of fatigue tests on vintage API Grade X52 steel in pure nitrogen, air and gaseous hydrogen at partial pressures of 1 and 207 bar. Circumferential notch tension (CNT) specimens with direct current potential difference (DCPD) measurements are used to get S–N curves for crack initiation and failure, and compact tension (CT) tests to assess crack growth rates. Results indicate that air accelerates crack initiation, low hydrogen partial pressure affects the crack growth rate, and higher pressures have the largest impact on both. Surprisingly, crack initiation is faster in air than at 1 bar hydrogen partial pressure. The CNT tests also reveal that the orientation of the banded microstructure has no effect on the crack initiation site, but it influences its growth behavior. Moreover, fractography shows that hydrogen also promotes instances of quasi-cleavage and intergranular fracture, linked to embrittlement of the material. These results demonstrate that, while hydrogen may impact the entirety of the fatigue process, its effects on the early stages of damage accumulation become relevant only at larger pressures. More comprehensive studies of crack initiation in hydrogen atmospheres will be critical to future codes and standards for hydrogen infrastructure.
energy & fuels,electrochemistry,chemistry, physical