Two low-firing microwave dielectric ceramics Na 2 LnMg 2 V 3 O 12 (Ln = Pr, Yb) and their chemical compatibility with silver

Minyu Xu,Huaicheng Xiang,Liang Fang,Ying Tang,Chunchun Li

DOI: https://doi.org/10.1007/s10854-017-7053-9

2017-01-01

Abstract:Two low-firing Na 2 LnMg 2 V 3 O 12 (Ln = Pr, Yb) ceramics were prepared by the conventional solid-state reaction method, and the sintering behavior, phase purity, and microwave dielectric properties were investigated. Both ceramics crystallized in a cubic garnet structure and could be well densified below 900 °C. Na 2 PrMg 2 V 3 O 12 sintered at 860 °C/4 h had ε r = 12.6, Q × f = 15,040 GHz, τ f = −45.1 ppm/°C, and Na 2 YbMg 2 V 3 O 12 possessed the optimum microwave dielectric properties with ε r = 13.1, Q × f = 22,040 GHz, τ f = −59.2 ppm/°C when sintered at 820 °C/4 h. LiCa 2 Mg 2 V 3 O 12 was chosen as a τ f compensator to tailor the thermal stability of Na 2 LnMg 2 V 3 O 12 due to the same structure and its large positive τ f value. Temperature-stable ceramics based on (1− x ) Na 2 LnMg 2 V 3 O 12 – x LiCa 2 Mg 2 V 3 O 12 were obtained with near-zero τ f values of +0.5 and −1.6 ppm/°C, respectively, when sintered at 820 °C/4 h. Both compounds did not react with the commonly used silver electrodes.