Local Liquation Phenomenon and Its Effect on Mechanical Properties of Joint in Friction Stir Welded 2219 Al Alloy

Kang Ju,Liang Suying,Wu Aiping,Li Quan,Wang Guoqing

DOI: https://doi.org/10.11900/0412.1961.2016.00311

IF: 1.797

2017-01-01

ACTA METALLURGICA SINICA

Abstract:Al alloy 2219 (AA2219) exhibits excellent mechanical properties in a wide temperature range from -250 degrees C to 250 degrees C, indicating great potential for application in aerospace structures. Compared to fusion welding, friction stir welding (FSW) could significantly improve mechanical properties of the AA2219 joints. Since invented by the welding institute (TWI) of UK in 1991, FSW has been treated as a solid-state joining technique by the commercial companies, which has been in an agreement in most scientific researchers. However, recently a controversy that has been raised over the viewpoint that FSW is a strict solid-state process, and some observations of liquation have been reported, especially in the stir zone of friction stir spot welding (FSSW) joint. However, the phenomenon of liquation in FSW AA2219 joints has not been reported previously. Therefore, the aim of this work is to reveal the evidence of local liquation during FSW AA2219-T8 and its effect on mechanical properties of the joints. In this work, AA2219-T8 plates ( 8 mm thick) were friction stir welded at a welding speed of 180 mm/min and a rotation speed of 800 r/min using a welding tool with threaded pin. Heat treatment and thermal simulation experiments were carried out to contrast the characteristics of the local liquation regions. A Vickers microhardness testing machine and an in situ SEM imaging tensile test facility were employed to study the effect of local liquation on mechanical properties of the joints. The results showed that the microstructures in the local liquation regions were divorced eutectic, and its formation was related to the coupled thermal-mechanical interaction during the FSW process. In the FSW process, the local high temperature led to constitutional liquation. During the cooling period, the semisolid mixtures decomposed into a(Al) matrices and theta(Al2Cu) particles under stir and material flow actions. The liquation regions had a lower value of hardness than the normal regions in the nugget zone ( NZ), making the liquidation region susceptible to cracks initiation and decreasing the ultimate tensile strength and elongation for a local liquation region contained NZ sample. However, the negative effect of local liquation regions on the mechanical properties of the FSW AA2219-T8 joint was less than that of the thermo-mechanically affected zone (TMAZ), since the local liquation regions were only localized and tiny fractions being in the NZ, whereas the TMAZ was whole softened.