A Comparative Degradation Study of Commercial Lithium-Ion Cells under Low-Temperature Cycling

Yakun Zhang,Hao Ge,Jun Huang,Zhe Li,Jianbo Zhang

DOI: https://doi.org/10.1039/c7ra02581e

IF: 4.036

2017-01-01

RSC Advances

Abstract:Severe deterioration of lithium-ion cells at low temperatures constitutes one of the bottlenecks for the wide adoption of electric vehicles.

What problem does this paper attempt to address?

Impact of Low Temperature Exposure on Lithium-Ion Batteries: A Multi-Scale Study of Performance Degradation, Predictive Signals and Underlying Mechanisms

Ke Chen,Jiayuan Luo,Yuqi Huang

DOI: https://doi.org/10.1016/j.cej.2024.158260

IF: 15.1

2024-01-01

Chemical Engineering Journal

Abstract:The rapid global expansion of electric vehicles and energy storage industries necessitates understanding lithium-ion battery performance under unconventional conditions, such as low temperature. This study investigates long-term capacity degradation of lithium-ion batteries after low temperature exposure subjected to various C-rate cycles. Findings reveal that low temperature exposure accelerates capacity degradation, especially with increased C-rates or longer exposure durations. A distinctive sunken region appears on the NMC H-stage peak as cycling progresses after low temperature exposure, indicating NMC particle damage and serving as a predictive signal for identifying low temperature exposure batteries. Electrochemical analyses and invasive detection indicate that low temperature exposure causes NMC particle cracking, leading to dead lithium generation. This dead lithium deposits on electrode surfaces, as well as the overconsumption of electrolyte, inhibiting reactions and reducing capacity. Additionally, dead lithium accumulates on separators, impeding ion transport and further accelerating capacity loss. NMC particle cracks develop faster after low temperature exposure due to stress concentration at internal slits. This stress concentration causes the maximum stress within the NMC particles to exceed tensile stress limits, resulting in rapid crack propagation. The internal cracks become larger with prolonged low temperature exposure, causing greater stress concentration and leading to faster crack propagation. Based on these insights, strategies from existing literature are discussed to mitigate the adverse impacts of low temperature exposure on lithium-ion battery performance and enhance the reliability and longevity of lithium-ion battery in extreme conditions.
Effect of Aging Path on Degradation Characteristics of Lithium-Ion Batteries in Low-Temperature Environments

Zhizu Zhang,Changwei Ji,Yangyi Liu,Yanan Wang,Bing Wang,Dianqing Liu

DOI: https://doi.org/10.3390/batteries10030107

2024-03-15

Batteries

Abstract:Typical usage scenarios for energy storage and electric vehicles (EVs) require lithium-ion batteries (LIBs) to operate under extreme conditions, including varying temperatures, high charge/discharge rates, and various depths of charge and discharge, while also fulfilling vehicle-to-grid (V2G) interaction requirements. This study empirically investigates the impact of ambient temperature, charge/discharge rate, and charge/discharge cut-off voltage on the capacity degradation rate and internal resistance growth of 18,650 commercial LIBs. The charge/discharge rate was found to have the most significant influence on these parameters, particularly the charging rate. These insights contribute to a better understanding of the risks associated with low-temperature aging and can aid in the prevention or mitigation of safety incidents.
The Dilemma of C-Rate and Cycle Life for Lithium-Ion Batteries under Low Temperature Fast Charging

Zhenhai Gao,Haicheng Xie,Xianbin Yang,Wanfa Niu,Shen Li,Siyan Chen

DOI: https://doi.org/10.3390/batteries8110234

2022-11-11

Batteries

Abstract:Electric vehicles (EVs) in severe cold regions face the real demand for fast charging under low temperatures, but low-temperature environments with high C-rate fast charging can lead to severe lithium plating of the anode material, resulting in rapid degradation of the lithium-ion battery (LIB). In this paper, by constructing an electrode–thermal model coupling solid electrolyte interphase (SEI) growth and lithium plating, the competition among different factors of capacity degradation under various ambient temperatures and C-rates are systematically analyzed. In addition, the most important cause of rapid degradation of LIBs under low temperatures are investigated, which reveal the change pattern of lithium plating with temperature and C-rate. The threshold value and kinetic law of lithium plating are determined, and a method of lithium-free control under high C-rate is proposed. Finally, by studying the average aging rate of LIBs, the reasons for the abnormal attenuation of cycle life at lower C-rates are ascertained. Through the chromaticity diagram of the expected life of LIBs under various conditions, the optimal fast strategy is explored, and its practical application in EVs is also discussed. This study can provide a useful reference for the development of high-performance and high-safety battery management systems to achieve fine management.
Impact of low temperature and charge profile on the aging of lithium-ion battery: Non-invasive and post-mortem analysis

Weixiong Wu,Ruixin Ma,Jizhen Liu,Min Liu,Weiliang Wang,Qian Wang

DOI: https://doi.org/10.1016/j.ijheatmasstransfer.2021.121024

IF: 5.2

2021-05-01

International Journal of Heat and Mass Transfer

Abstract:In this paper, the low temperature performance of lithium-ion batteries under various charge rates ranged from 0.2 C to 1 C were studied. To shed some light on the degradation modes and aging mechanism, non-invasive and post-mortem analysis were adopted. The results reveal that there is a considerable reversible capacity loss and internal resistance increase with the increase in charge rate. Particularly, the relative capacity of 1C charged cell after 150 cycles is below 0.8, indicating the end of life is achieved. In addition, the increased internal resistance will lead to a substantial increase in heat generation rate, which is an important factor to the thermal safety control of battery related to the design of thermal management strategy. Besides the resistance increase, two major degradation modes i.e., loss of lithium inventory and loss of active material are demonstrated according to the differential voltage and incremental capacity analysis. It is found that lithium plating is regarded as the main aging mechanism. The anode material of cycled cell display distinct deterioration even exfoliated from the copper foil upon a macroscopic check, and a thick deposited layer morphology and cracking of the layer is visible from a micro point of view through cell opening. During the low temperature charging, lithium plating could be triggered due to the limitation of charge transfer resulted from high-rate charge as well as the limitation of solid-state diffusion resulted from low temperature. The continuous lithium-consuming during cycling will lead to secondary SEI formation, which may result in dead lithium and stripping, eventually reversible capacity loss.

engineering, mechanical,thermodynamics,mechanics
A Comparative Study on the Degradation Behaviors of Overcharged Lithium‐ion Batteries under Different Ambient Temperatures

Dongxu Ouyang,Mingyi Chen,Jingwen Weng,Jian Wang

DOI: https://doi.org/10.1002/er.4996

IF: 4.6

2019-01-01

International Journal of Energy Research

Abstract:In the current work, a series of experiments are carried out to investigate the degradation behavior of lithium-ion batteries during overcharge cycling, as well as the influence of ambient temperature on the degradation. In which, different charge cut-off voltages (4.5, 4.8, and 5.0 V) and ambient temperatures (0 degrees C, 20 degrees C, 50 degrees C, and 70 degrees C) are included. During the overcharge process, the batteries demonstrate severe temperature rises, and several key electrochemical parameters such as the charge capacity, energy density, median voltage, and resistances all increase, revealing the deterioration of heat generation and electrode kinetics. Besides that, batteries exhibit serious degradation behavior during the overcharge cycling, which is presented through the evolution of battery temperature curves, charge voltage curves, and internal resistance curves. Moreover, the severity of degradation exacerbates with the increasing overcharge degree. Finally, it is found that deep-overcharged batteries may be more sensitive to the ambient temperature than slight-overcharged ones, where an abusive temperature can significantly aggravate the corresponding degradation.
Effects of Low-Temperature Pre-Cycling on High-Temperature Degradation of Lithium-Ion Cells

Muriel Carter,Pragati Poudel,Megan Gober,Boryann Liaw,George J. Nelson,Guangsheng Zhang,Boryann (Bor Yann) Liaw

DOI: https://doi.org/10.1149/ma2023-012624mtgabs

2023-08-28

ECS Meeting Abstracts

Abstract:Lithium-ion (Li-ion) batteries suffer accelerated degradation when the operating temperature is beyond the optimal range 1, 2 , about 20 °C to 35 °C. At lower temperatures and higher temperatures, lithium plating and solid-electrolyte interface (SEI) growth are dominating degradation mechanisms, respectively 1 . A previous work by our group 3 showed interestingly that pre-cycling Li-ion cells at 5 °C reduced degradation during cycling at higher temperatures of 45 °C and 60 °C. The observation suggested that low-temperature pre-cycling has significant effects on high-temperature degradation of Li-ion cells. The previous work was based on small cells that consisted of a single pair of electrodes. To confirm if the phenomenon also exists in large cells that consist of multiple pairs of electrodes, commercially available 3-Ah pouch cells are tested. It is found that pre-cycling of these large cells at 5 °C also significantly reduces their degradation at 45 °C. However, this effect is observed only when the cells are compressed. Without compression, cells pre-cycled at 5 °C degrade much faster than baseline cells cycled only at 45 °C. Further analysis of the results, such as cell internal resistance analysis and electrochemical impedance spectroscopy, is performed to better understand the effects of low-temperature pre-cycling on high-temperature degradation behaviors of Li-ion cells. References: T. Waldmann, M. Wilka, M. Kasper, M. Fleischhammer and M. Wohlfahrt-Mehrens, Journal of Power Sources , 262 , 129 (2014). F. Leng, C. M. Tan and M. Pecht, Scientific Reports , 5 , 12967 (2015). P. Poudel, Z. Du, B. Liaw, T. Iriyama and G. Zhang, ECS Meeting Abstracts , MA2022-01 , 443 (2022).
Experimental analysis of commercial LiFePO4 battery life span used in electric vehicle under extremely cold and hot thermal conditions

G. R. Molaeimanesh,S. M. Mousavi-Khoshdel,A. B. Nemati

DOI: https://doi.org/10.1007/s10973-020-09272-z

IF: 4.755

2020-01-18

Journal of Thermal Analysis and Calorimetry

Abstract:To widely commercialize electric vehicles more efforts for their life improvement seem extremely inevitable. Thermal conditions can have profound and nonlinear effects on the degradation rate of an electric vehicle battery pack as well as its performance and safety level. In the current study, both cycle life and calendar life of a commercial LiFePO4 cell are investigated experimentally by means of capacity fading and resistance increment evaluation for 4 different thermal conditions from extremely cold condition of − 20 °C—which is not well studied in the literature—till hot condition of 55 °C. The calendar life tests show that the best condition for storing cells is at 5 °C and 50% SOC and the cycle life tests demonstrate that the best operating temperature is 25 °C based on the dynamic stress test discharge/charge profile (a test profile for electric vehicles). It is also found that the capacity fading and resistance increment at a high temperature such as 50 °C are destructively significant. The presented curves in this paper can also serve as an aging data source for further work on battery lifetime modeling and diagnostics. The role of temperature on the degradation level is also discovered via scanning electron microscopy.

chemistry, physical, analytical,thermodynamics
Effects of Non-Uniform Temperature Distribution on Degradation of Lithium-Ion Cells

Guangsheng Zhang

DOI: https://doi.org/10.1149/ma2018-01/3/364

2018-01-01

ECS Meeting Abstracts

Abstract:Lithium-ion cells degrade much faster at temperatures higher than 25 °C mainly due to accelerated solid-electrolyte interface (SEI) growth in anode and degeneration of cathode [1, 2]. It is also known that temperature distributions in lithium-ion cells are not uniform [3] due to very low thermal conductivity of battery materials. The non-uniform temperature distributions could cause non-uniform degradation, thus exacerbating the thermal degradation problem, especially for large-format lithium-ion cells during high power operation. The effects of non-uniform temperature distributions on degradation of lithium-ion cells will be investigated and progress will be presented. References [1] C.Y. Wang, G. Zhang, S. Ge, T. Xu, Y. Ji, X.G. Yang, Y. Leng. Lithium-ion battery structure that self-heats at low temperatures, Nature, 529(7587) (2016) 515-518. [2] T. Waldmann, M. Wilka, M. Kasper, M. Fleischhammer, M. Wohlfahrt-Mehrens. Temperature dependent ageing mechanisms in lithium-ion batteries – A post-mortem study, Journal of Power Sources, 262 (2014) 129-135. [3] G. Zhang, L. Cao, S. Ge, C.Y. Wang, C.E. Shaffer, C.D. Rahn. In situ measurement of radial temperature distributions in cylindrical Li-ion cells, Journal of The Electrochemical Society, 161(10) (2014) A1499-A1507.
Influence of charge rate on the cycling degradation of LiFePO 4 /mesocarbon microbead batteries under low temperature

Yong Zheng,Yan-Bing He,Kun Qian,Dongqing Liu,Qingwen Lu,Baohua Li,Xindong Wang,Jianling Li,Feiyu Kang

DOI: https://doi.org/10.1007/s11581-017-2032-y

IF: 2.961

2017-01-01

Ionics

Abstract:The lithium-ion batteries show extremely poor cycling performance at low temperature. The main degradation mechanism is not clear. To address the fading mechanism, the cycling degradation of commercial LiFePO 4 /mesocarbon microbead (MCMB) batteries under various charge rate (1/10C, 1/3C, 1/2C, and 1C) at −10 °C is systematically investigated using nondestructive tests combining with post-mortem analysis. The low-temperature charging under high charge rates of 1/3C, 1/2C, and 1C results in severe lithium plating, which leads to extremely serious capacity loss. In contrast, no lithium plating occurred under low charge rate of 1/10C. The lithium plating on the anode surface leads to consumption of active lithium ions and electrolyte, which causes the capacity decay and increases ohmic resistance ( R b ) with cycling number under high charge rates. The lithium plating on the anode surface is partially reversible, which brings about the capacity recovery of batteries after 80 cycles at 25 °C. The above results are proved by the followed post-mortem measurements. The evolution of the surface morphologies of MCMB electrodes upon cycling shows that a layer composed of rod-like lithium is formed on the anode surface.
Degradation in LiFePO4 Composite Cathodes of Lithium-ion Batteries for Electric Vehicles

WANG Luo-ying,LI Jian-ling,GAO Fei,WANG Xin-dong,ZHAO Shu-hong,WANG Zi-dong

DOI: https://doi.org/10.3969/j.issn.1001-0211.2011.01.014

2011-01-01

Abstract:Coin cells are assembled with positive electrode of LiFePO4 commercial battery,and the accelerated cycle life test with two factors of temperature and discharge rate are conducted.The results indicate that in early aging,both capacity and power performances are firstly increased and then degraded.The electrochemical reaction is accelerated by high temperature,otherwise Li-ion diffusion coefficient seems not temperature-sensitive.The cells aging is accelerated by high discharge rate,which enhances the polarization.
Unrevealing the effects of low temperature on cycling life of 21700-type cylindrical Li-ion batteries

Daozhong Hu,Gang Chen,Jun Tian,Ning Li,Lai Chen,Yuefeng Su,Tinglu Song,Yun Lu,Duanyun Cao,Shi Chen,Feng Wu

DOI: https://doi.org/10.1016/j.jechem.2020.12.024

IF: 13.1

2021-09-01

Journal of Energy Chemistry

Abstract:The low-temperature performance of Li-ion batteries (LIBs) has important impacts on their commercial applications. Besides the metallic lithium deposition, which is regarded as one of the main failure mechanisms of the LIBs at low temperatures, the synergistic effects originating from the cathode, anode, electrolyte, and separators to the batteries are still not clear. Here, the 21700-type cylindrical batteries were evaluated at a wide range of temperatures to investigate the failure mechanism of batteries. Voltage relaxation, and the post-mortem analysis combined with the electrochemical tests, unravel that the capacity degradation of batteries at low temperature is related to the lithium plating at graphite anodes, the formation of unsatisfied solid deposited/decomposed electrolyte mixture phase on the anode, the precipitation of solvent in the electrolytes and the block of separator pores, and the uneven dissolved transition metal-ions from the cathode. We hope this finding may open up a new avenue to alleviate the capacity degradation of advanced LIBs at low temperatures and shed light on the development of outstanding low-temperature LIBs via simultaneous optimization of all the components including electrodes, electrolytes and separators.

chemistry, physical,engineering, chemical, applied,energy & fuels
Lithium-Ion Batteries under Low-Temperature Environment: Challenges and Prospects

Hanwu Luo,Yuandong Wang,Yi-Hu Feng,Xin-Yu Fan,Xiaogang Han,Peng-Fei Wang

DOI: https://doi.org/10.3390/ma15228166

IF: 3.4

2022-11-17

Materials

Abstract:Lithium-ion batteries (LIBs) are at the forefront of energy storage and highly demanded in consumer electronics due to their high energy density, long battery life, and great flexibility. However, LIBs usually suffer from obvious capacity reduction, security problems, and a sharp decline in cycle life under low temperatures, especially below 0 °C, which can be mainly ascribed to the decrease in Li+ diffusion coefficient in both electrodes and electrolyte, poor transfer kinetics on the interphase, high Li+ desolvation barrier in the electrolyte, and severe Li plating and dendrite. Targeting such issues, approaches to improve the kinetics and stability of cathodes are also dissected, followed by the evaluation of the application prospects and modifications between various anodes and the strategies of electrolyte design including cosolvent, blended Li salts, high-concentration electrolyte, and additive introduction. Such designs elucidate the successful exploration of low-temperature LIBs with high energy density and long lifespan. This review prospects the future paths of research for LIBs under cold environments, aiming to provide insightful guidance for the reasonable design of LIBs under low temperature, accelerating their widespread application and commercialization.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
Review on Low-Temperature Electrolytes for Lithium-Ion and Lithium Metal Batteries

Sha Tan,Zulipiya Shadike,Xinyin Cai,Ruoqian Lin,Atsu Kludze,Oleg Borodin,Brett L. Lucht,Chunsheng Wang,Enyuan Hu,Kang Xu,Xiao-Qing Yang

DOI: https://doi.org/10.1007/s41918-023-00199-1

IF: 31.3

2023-11-28

Electrochemical Energy Reviews

Abstract:Abstract Among various rechargeable batteries, the lithium-ion battery (LIB) stands out due to its high energy density, long cycling life, in addition to other outstanding properties. However, the capacity of LIB drops dramatically at low temperatures (LTs) below 0 °C, thus restricting its applications as a reliable power source for electric vehicles in cold climates and equipment used in the aerospace. The electrolyte engineering has proved to be one of the most effective approaches to mitigate LIB performance degradation at LTs. In this review, we summarize the important factors contributing to the deterioration in Li + transport and capacity utilization at LTs while systematically categorize the solvents, salts and additives reported in the literature. Strategies to improve the Li + transport kinetics, in the bulk electrolyte and across the interphases, are discussed. In particular, the formation mechanism of solid electrolyte interphase and its functionality for LT electrolytes are analyzed. Perspectives on the future evolution of this area are also provided. Graphical abstract

electrochemistry
Lithium plating on the anode for lithium-ion batteries during long-term low temperature cycling

Guangxu Zhang,Xuezhe Wei,Guangshuai Han,Haifeng Dai,Jiangong Zhu,Xueyuan Wang,Xuan Tang,Jiping Ye

DOI: https://doi.org/10.1016/j.jpowsour.2020.229312

IF: 9.2

2021-02-01

Journal of Power Sources

Abstract:Occurrence of lithium plating on the anode is a severe side reaction in the lithium-ion batteries, which brings cell capacity degradation and reduces the cell safety. This paper focuses on 37Ah commercial lithium-ion batteries and clarifies the evolution of lithium plating during long-term low temperature (−10 °C) cycling. The tested cells are analyzed at different degradation stages, named "fixed-point analysis", to evaluate the evolution process of lithium plating. It is found that the capacity fade and the internal resistance increase exhibit a decelerated trend with a turning point around 450 cycles. The loss of cyclable lithium caused by lithium plating is deemed to be the main reason behind the battery degradation. Post-mortem analysis including scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS) is conduced to reveal the mechanism. The thickness and morphology change of plated lithium, and the plated lithium covered by solid electrolyte interface film, are disclosed by the surface and cross-section SEM images from the fixed-point analysis. XPS analysis further reveals the composition of solid electrolyte interface film, and the plated lithium existing. In a nutshell, lithium plating is inhomogeneous and has high spatial dependence.

energy & fuels,materials science, multidisciplinary,electrochemistry,chemistry, physical
Electrochemical and Thermal Characteristics of Aging Lithium-Ion Cells after Long-Term Cycling at Abusive-Temperature Environments

Dongxu Ouyang,Jingwen Weng,Mingyi Chen,Jian Wang,Zhirong Wang

DOI: https://doi.org/10.1016/j.psep.2022.01.055

IF: 7.8

2022-01-01

Process Safety and Environmental Protection

Abstract:This work prepares five kinds of cell samples, i.e. the fresh cell, the cell degrades to 90% SOH (state of health) after high-temperature cycling, the cell degrades to 80% SOH after high-temperature cycling, the cell degrades to 90% SOH after low-temperature cycling and the cell degrades to 80% SOH after low-temperature cycling to reveal the electrochemical and thermal characteristics of the aging cells induced by abusive-temperature cycling. The cells under abusive-temperature environments show severe degradation behaviors over cycling, which may be mainly attributed to lithium inventory loss, anode material loss and electrode interface deterioration. Besides that, abusive-temperature cycling affects the thermal stability of positive electrode materials and single cells, and this is related with environmental temperatures. By comparison to the fresh cell, the thermal stability of the positive electrode materials and single cells after high-temperature cycling is improved, which is different from that of the low-temperature cycled ones who illustrate deteriorated thermal safety at elevated temperatures. Therefore, the thermal risk of aging cells after long-term low-temperature cycling is worthy of more concern, the according monitor and/or management of these cells during operation, transportation, storage and recycle, etc. should be valued.
Challenges and development of lithium-ion batteries for low temperature environments

Nan Piao,Xuning Gao,Huicong Yang,Zhenqiang Guo,Guangjian Hu,Hui-Ming Cheng,Feng Li

DOI: https://doi.org/10.1016/j.etran.2021.100145

IF: 11.9

2022-02-01

eTransportation

Abstract:Lithium-ion batteries (LIBs) play a vital role in portable electronic products, transportation and large-scale energy storage. However, the electrochemical performance of LIBs deteriorates severely at low temperatures, exhibiting significant energy and power loss, charging difficulty, lifetime degradation, and safety issue, which has become one of the biggest challenges for LIBs. This article aims to review challenges and limitations of the battery chemistry in low-temperature environments, as well as the development of low-temperature LIBs from cell level to system level. This review introduces feasible solutions to accelarate low-temperature kinetics by increasing the inherent reactivity from cell design and improving the external reaction temperature from heating techniques. In addition, real-time and accurate monitoring of the battery temperature for the battery thermal management, as well as the optimization of charging protocols and the online lithium-plating monitoring in battery management systems are outlined. In general, a systematic review of low-temperature LIBs is conducted in order to provide references for future research.

English Else
A comparative study of commercial lithium ion battery cycle life in electrical vehicle: Aging mechanism identification

Xuebing Han,Minggao Ouyang,Languang Lu,Jianqiu Li,Yuejiu Zheng,Zhe Li

DOI: https://doi.org/10.1016/j.jpowsour.2013.11.029

IF: 9.2

2014-01-01

Journal of Power Sources

Abstract:When lithium-ion batteries age with cycling, the battery capacity decreases and the resistance increases. The aging mechanism of different types of lithium-ion batteries differs. The loss of lithium inventory, loss of active material, and the increase in resistance may result in battery aging. Generally, analysis of the battery aging mechanism requires dismantling of batteries and using methods such as X-ray diffraction and scanning electron microscopy. These methods may permanently damage the battery. Therefore, the methods are inappropriate for the battery management system (BMS) in an electric vehicle. The constant current charging curves while charging the battery could be used to get the incremental capacity and differential voltage curves for identifying the aging mechanism; the battery state-of-health can then be estimated. This method can be potentially used in the BMS for online diagnostic and prognostic services. The genetic algorithm could be used to quantitatively analyze the battery aging offline. And the membership function could be used for onboard aging mechanism identification.
Experimental Study on High-Temperature Cycling Aging of Large-Capacity Lithium Iron Phosphate Batteries

Zhihang Zhang,Languang Lu,Yalun Li,Hewu Wang,Minggao Ouyang

DOI: https://doi.org/10.1088/1742-6596/2584/1/012046

2023-09-28

Journal of Physics Conference Series

Abstract:Large-capacity lithium iron phosphate (LFP) batteries are widely used in energy storage systems and electric vehicles due to their low cost, long lifespan, and high safety. However, the lifespan of batteries gradually decreases during their usage, especially due to internal heat generation and exposure to high temperatures, which leads to rapid capacity degradation. In-depth research is needed on the degradation characteristics of large-capacity LFP batteries under high temperatures. To study the degradation characteristics of large-capacity LFP batteries at high temperatures, a commercial 135Ah LFP battery is selected for 45°C high-temperature dynamic cycling aging experiments and 25°C reference performance experiments. A detailed analysis of the degradation process is conducted by examining the patterns of changes in charge-discharge voltage curves, capacity, internal resistance, open circuit voltage (OCV), and incremental capacity curve. The study uncovers that the OCV displays diverse degradation patterns at different states of charge (SOC). Furthermore, it identifies the loss of lithium inventory and active material as the fundamental factors contributing to the degradation observed during high-temperature cycling. This study provides references for developing battery life prediction algorithms and designing long-cycle-life battery cells.
A Review on Low-Temperature Performance Management of Lithium-Ion Batteries

Jincheng Zhan,Yifei Deng,Yaohui Gao,Jiaoyi Ren,Yuang Liu,Shun Rao,Weifeng Li,Zhenhai Gao,Yupeng Chen

DOI: https://doi.org/10.1115/1.4063611

IF: 2.323

2023-10-26

Journal of Electrochemical Energy Conversion and Storage

Abstract:Abstract Lithium-ion batteries (LIBs) are widely used in electric vehicles, energy storage power stations and other portable devices for their high energy densities, long cycle life, and low self-discharge rate. However, they still face several challenges. Low-temperature environments have slowed down the use of LIBs by significantly deteriorating their normal performance. This review aims to resolve this issue by clarifying the phenomenon and reasons for the deterioration of LIB performance at low temperatures. From the perspective of system management, this review summarizes and analyzes the common performance-improving methods from two aspects including preheating and charging optimization and then depicts the future development of methods in this regard. This review is expected to inspire further studies for the improvement of the LIB performance at low temperatures.

energy & fuels,electrochemistry
A Comparative Study of Commercial Lithium Ion Battery Cycle Life in Electric Vehicle: Capacity Loss Estimation

Xuebing Han,Minggao Ouyang,Languang Lu,Jianqiu Li

DOI: https://doi.org/10.1016/j.jpowsour.2014.06.111

IF: 9.2

2014-01-01

Journal of Power Sources

Abstract:Now the lithium ion batteries are widely used in electric vehicles (EV). The cycle life is among the most important characteristics of the power battery in EV. In this report, the battery cycle life experiment is designed according to the actual working condition in EV. Five different commercial lithium ion cells are cycled alternatively under 45 degrees C and 5 degrees C and the test results are compared. Based on the cycle life experiment results and the identified battery aging mechanism, the battery cycle life models are built and fitted by the genetic algorithm. The capacity loss follows a power law relation with the cycle times and an Arrhenius law relation with the temperature. For automotive application, to save the cost and the testing time, a battery SOH (state of health) estimation method combined the on-line model based capacity estimation and regular calibration is proposed. (C) 2014 Elsevier B.V. All rights reserved.

A Comparative Degradation Study of Commercial Lithium-Ion Cells under Low-Temperature Cycling

Impact of Low Temperature Exposure on Lithium-Ion Batteries: A Multi-Scale Study of Performance Degradation, Predictive Signals and Underlying Mechanisms

Effect of Aging Path on Degradation Characteristics of Lithium-Ion Batteries in Low-Temperature Environments

The Dilemma of C-Rate and Cycle Life for Lithium-Ion Batteries under Low Temperature Fast Charging

Impact of low temperature and charge profile on the aging of lithium-ion battery: Non-invasive and post-mortem analysis

A Comparative Study on the Degradation Behaviors of Overcharged Lithium‐ion Batteries under Different Ambient Temperatures

Effects of Low-Temperature Pre-Cycling on High-Temperature Degradation of Lithium-Ion Cells

Experimental analysis of commercial LiFePO4 battery life span used in electric vehicle under extremely cold and hot thermal conditions

Effects of Non-Uniform Temperature Distribution on Degradation of Lithium-Ion Cells

Influence of charge rate on the cycling degradation of LiFePO 4 /mesocarbon microbead batteries under low temperature

Degradation in LiFePO4 Composite Cathodes of Lithium-ion Batteries for Electric Vehicles

Unrevealing the effects of low temperature on cycling life of 21700-type cylindrical Li-ion batteries

Lithium-Ion Batteries under Low-Temperature Environment: Challenges and Prospects

Review on Low-Temperature Electrolytes for Lithium-Ion and Lithium Metal Batteries

Lithium plating on the anode for lithium-ion batteries during long-term low temperature cycling

Electrochemical and Thermal Characteristics of Aging Lithium-Ion Cells after Long-Term Cycling at Abusive-Temperature Environments

Challenges and development of lithium-ion batteries for low temperature environments

A comparative study of commercial lithium ion battery cycle life in electrical vehicle: Aging mechanism identification

Experimental Study on High-Temperature Cycling Aging of Large-Capacity Lithium Iron Phosphate Batteries

A Review on Low-Temperature Performance Management of Lithium-Ion Batteries

A Comparative Study of Commercial Lithium Ion Battery Cycle Life in Electric Vehicle: Capacity Loss Estimation