Abstract:To investigate the compressive behavior of concrete under a freeze-thaw environment, porosity swelling theory, a damaged plastic model, and an element removal technique are combined to propose a novel mesoscopic numerical model of concrete. The porosity swelling theory is employed to represent the pores evolution behavior of concrete under freeze-thaw cycles, and a novel calculation method for porosity expansion is presented to characterize freeze-thaw cycle times. The damaged plastic model is used to describe the tensile and compressive features of the mortar and interface transition zone. The element removal technique with maximum damage criterion is employed to implement crack propagation. It was demonstrated that the model could capture the freeze-thaw damage and compressive failure of concrete well. The uniaxial compressive behavior of five random mesonumerical models of freeze-thaw concrete was investigated. The results showed that freeze-thaw cycles can cause tensile damage to the mortar near pores and the spalling of surface mortar. With the increase of concrete freeze-thaw cycles, the dispersion degree of the compressive stress–strain curve gradually rises, and the peak stress and peak strain of the freeze-thaw concrete stress–strain curve decrease and increase, respectively. During the freeze-thaw cycles, the sustained preload will decrease the compressive strength because it causes the microcracks to accelerate the damage induced by the freeze-thaw cycles. Then, the influence of mortar and interface transition zone properties on the compressive strength of concrete under freeze-thaw cycles was analyzed. Under 100 freeze-thaw cycles, the maximum attenuation rates of concrete compressive strength increase by 9.39% and 34.26% with the increase of interface transition zone and mortar properties, respectively. Increasing mortar properties and decreasing the sustained preload will enhance the ability of concrete to resist freeze-thaw cycles.

Mesoscopic Damage Model of Concrete Subjected to Freeze-Thaw Cycles Using Mercury Intrusion Porosimetry and Differential Scanning Calorimetry (MIP-DSC)

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

Mesoscale Simulation of Fatigue Behavior of Concrete Materials Damaged by Freeze-Thaw Cycles

Mesoscale Simulation of Concrete Behavior with Non-Uniform Frost Damage with Verification by CT Imaging

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Study on the Damage Mechanism of Pore Structure in Concrete Subjected to Freeze-Thaw Cycles

A stochastic damage model for evaluating the internal deterioration of concrete due to freeze–thaw action

Meso-scale mechanical model for mortar deformation under freeze thaw cycles

Structural behaviors evaluation of RC beam under frost damage - A methodology with meso-macro material/bond simulation and integrating into structural analysis

Mesoscale Simulation of Deformation for Mortar and Concrete under Cyclic Freezing and Thawing Stress

Modeling and Mesoscale Simulation of Ice-Strengthened Mechanical Properties of Concrete at Low Temperatures

Microstructural Damage Evolution And Its Effect On Fracture Behavior Of Concrete Subjected To Freeze-Thaw Cycles

Three-Dimensional Mesonumerical Model of Freeze-Thaw Concrete Based on the Porosity Swelling Theory

Meso-Scale Failure of Freezing–Thawing Damage of Concrete under Uniaxial Compression

Degradation Mechanism and Numerical Simulation of Pervious Concrete under Salt Freezing-Thawing Cycle

Experimental Examination of Electrical Characteristics for Portland Cement Mortar Frost Damage Evaluation

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Microstructural Damage Characterization Of Concrete Under Freeze-Thaw Action

3D mesoscale analysis of concrete containing defect damages during different freeze-thaw cycles