New Preparation Process of Long Afterglow Phosphor Eu and Dy Co-doped SrAl2O4
Jin HU,Jia-lin SUN,Jian-liang LIU,An SHI,Mao XU,Qin-qin GAO
DOI: https://doi.org/10.3321/j.issn:1000-7032.2006.02.008
2006-01-01
Chinese Journal of Luminescence
Abstract:The activated Al-Sr alloy powder was put immediately into boiling pure water,with liquid-solid(ratio) of 4 ∶1.The system was kept isothermal and stirred until white hydrolysates appears.The hydrolysates contain the mixture of Sr(OH)_2·8H_2O and Al(OH)_3 in main,included a little Al(OH)_3,AlOOH,SrCO_3,and 3SrO·Al_2O_3· 6H_2O.After heat treatment at 700 ℃ for 1 h,the mixture of SrO and α-Al_2O_3,γ-Al_2O_3 were formed.As a precursor,the hydrolysates after heat treatment had been used to prepare long after phosphor Eu,Dy co-doped SrAl_2O_4 at 1 300 ℃ for 1 h.The crystal structure of hydrolysates and Eu,Dy co-doped SrAl_2O_4 were analyzed by XRD.The luminescent properties of long afterglow material were studied.The(results) showed that the crystal structure of phosphor is β phase SrAl_2O_4,the emission spectra of Eu and Dy co-doped SrAl_2O_4 lied near 520 nm,resulted from the character transition of 4f5d-4f of Eu~(2+) ion.The method can improve afterglow properties dramatically.The initial luminescent intensity of long afterglow material reached 18 cd/m~2,and the duration time lasted 46 h.The improved properties are related to precipitation mechanism of AlSr alloy hydrolysates.With this procedure,SrO and Al_2O_3 will disperse evenly to effectively enlarge the contact area of the components,shorten the diffusive distance.As a result the sintering temperature could be decreased,while the reaction speed and the long afterglow fluorescent properties of the materials could be improved.