Microstructure and Mechanical Properties of the Laser-Welded Mg-3nd-0.2zn-0.4zr (nz30k) Magnesium Alloy

Keng Yan,Jinsong Su,Yong Zhao

DOI: https://doi.org/10.1016/j.optlastec.2017.02.002

2017-01-01

Abstract:This study aimed to investigate the microstructure and mechanical properties of the laser-welded Mg-3Nd-0.2Zn-0.4Zr (NZ30K) magnesium alloy. A fiber optic laser was used to weld 4-mm-thick Mg-3Nd-0.2Zn-0.4Zr (NZ30K) and AZ31 magnesium alloy plates. The microstructures of NZ30K and AZ31 joints were compared, and the distribution of Nd in NZ30K was emphatically investigated. Besides, microhardness distributions and tensile properties of NZ30K and AZ31 joints at room temperature and high temperature (200 degrees C) were tested, and fracture features were observed and analyzed. The results indicated that the NZ30K rare-earth magnesium alloy showed better properties especially at a high temperature (200 degrees C), benefiting from the strengthening phase, compared with the AZ31 joint, such as high temperature tensile strength, creep resistance at high temperature, and corrosion resistance. The micro hardness in the fusion zone of NZ30K changed a little compared with that in base metal, while the micro hardness in the fusion zone of AZ31 decreased significantly. The grain of NZ30K in the fusion zone was significantly refined with strengthening-phase distribution on the grain boundary. The tensile strength of NZ30K laser beam-welded joints at a high temperature (200 degrees C) decreased by 29% compared with that at room temperature, while the tensile strength of AZ31 joint at a high temperature (200 degrees C) decreased by 53% compared with that at room temperature, which was mainly because of the stable existence of the strengthening-phase Mg12Nd in the NZ30K rare-earth magnesium alloy while the strengthening-phase Mg17Al12 in AZ31 would soften and coarsen with the rise in temperature. (C) 2017 Elsevier Ltd. All rights reserved.