Abstract:Heterogeneous Ziegler–Natta and homogeneous metallocene catalysts are known to produce ultrahigh molecular weight polyethylene (UHMWPE) in the entangled state. On the other hand, only (two) homogeneous single-site catalysts are reported to yield disentangled UHMWPE (dis-UHMWPE). This disparity between the two types of catalysts and the two states of polyethylene can be bridged if a heterogeneous single-site catalyst that can yield dis-UHMWPE is made accessible. Here, one-pot two-step synthesis of a MgCl2 supported [Ti(OEt)4] derived catalyst 1 with a two-stage activation strategy is reported to produce dis-UHMWPE. Second activation of catalyst 1 was performed by adding excess modified methylaluminoxane (MMAO12), and XPS analysis indicated that the catalyst existed in only Ti(III) state at [Al]/[Ti] ratio of 600. Catalyst 1 after second activation with MMAO12 was found to be highly active in ethylene polymerization and produced dis-UHMWPE. Polymerization conditions were tailored to obtain molecular weight (M w) as high as 13 million g/mol PE. To the best of our knowledge, this is the first time a heterogeneous catalyst (catalyst 1) that displays pseudosingle site nature is able to produce dis-UHMWPE. The thus-prepared nascent polyethylene revealed a melting temperature of 141–144 °C, which is a characteristic melting transition for a dis-UHMWPE. The disentangled state of the nascent PE and its M w and MWD were further authenticated by rheological investigations. Isothermal time sweep oscillatory experiments in linear viscoelastic limit revealed a rapid rise in elastic modulus followed by equilibration to plateau modulus, which are characteristic features of the disentangled state. Thus, a pseudo-single-site heterogeneous catalyst has been accessed, which upon second activation with excess MMAO12 led to the production of dis-UHMWPE.

The First Vanadium-Oxide-Based UHMWPE Catalyst Supported on Chemically Modified Silica Gel

UHMWPE with Short‐chain Branches Synthesized by Alkenyl Substituted Phenoxy–imine Catalysts in Ethylene Polymerization

Remarkable Promotion Effect of Sulfation over the SiO2-Supported Vanadium-Oxide-Based Catalysts for UHMWPE

PREPARATION OF ULTRA HIGH MOLECULAR WEIGHT POLYETHYLENE USING STRUCTURED NANOPARTICAL ZIEGLER-NATTA CATALYSTS

Advanced Catalyst Technology for Broad/Bimodal Polyethylene, Achieved by Polymer-Coated Particles Supporting Hybrid Catalyst

Ethylene Polymerization with Palygorskite Supported Nickel-Diimine Catalyst

Solvent-free preparation of well-dispersed and highly active CrOx/VOx/TiO2-SiO2 bimetallic catalyst for bimodal UHMWPE/ HDPE in-reactor blends

Characteristics of Palygorskite Supported Cp_2 TiCl_2 Catalysts for Ethylene Polymerization

Study of Silica‐Supported Chromocene Catalysts for Ethylene Polymerization

Study of the effect of the nature of catalyst systems on the molecular structure and properties of ultra-high molecular weight polyethylene

Efficient Synthesis Of Low-Polydispersity Uhmwpe By Elevating Active Sites On Anchored Poss Molecules

Influence of Modified Ziegler–Natta Catalyst on the Entanglement Behavior and Properties of Ultrahigh-Molecular-Weight Polyethylene (UHMWPE)

A Novel Catalytic System of [O,O] Bidentate Titanium Complexes and Et2AlCl/Bu2Mg for the Production of Ultra‐High Molecular Weight Polyethylene

Vanadium Modification Effects on the (Sio2/mgo/mgcl2)•ticlxziegler-Natta Polyethylene Catalyst

Preparation and Characterization of Novel Polyethylene Supported Metallocene Catalysts

Novel SiO2‐Supported Chromocene and Vanadium Bimetallic Catalysts Producing Bimodal Polyethylene

Judicious Reduction of Supported Ti Catalyst Enables Access to Disentangled Ultrahigh Molecular Weight Polyethylene

Novel SiO2‐Supported Chromium Oxide/Chromocene Dual Site Catalysts for Synthesis of Bimodal UHMWPE/HDPE in Reactor Alloys

Novel SiO2‐Supported Chromium Oxide(Cr)/Vanadium Oxide(V) Bimetallic Catalysts for Production of Bimodal Polyethylene

Synthesis of Polyethylene with Bimodal Molecular Weight Distribution by Supported Iron‐based Catalyst

Enhanced properties of polyethylene through in situ polymerization with siloxene‐supported vanadium‐based catalysts