Mechanical and tribological properties of Zr–Cu–Ni–Al bulk metallic glasses with dual-phase structure
Qing Zhou,Weichao Han,Dawei Luo,Yin Du,Jiyang Xie,Xian-Zong Wang,Qiguang Zou,Xiaoxing Zhao,Haifeng Wang,Ben D. Beake
DOI: https://doi.org/10.1016/j.wear.2021.203880
IF: 4.695
2021-06-01
Wear
Abstract:<p>The effect of Fe addition on the structure, mechanical and wear properties of Zr–Cu–Ni–Al bulk metallic glasses (BMGs) was systematically investigated by thermal analysis, transmission electron microscopy (TEM), the compression test, the pin-on-disk macroscopic wear test and the microscopic nanoscratch test. TEM observation revealed the formation of a second glassy phase with a few nanometers in diameter in the Zr<sub>63.6-<em>x</em></sub>Cu<sub>18</sub>Ni<sub>10.4</sub>Al<sub>8</sub>Fe<sub><em>x</em></sub> (<em>x</em> = 1, 3, 5) BMGs. The results of the mechanical tests showed that although compression strength and hardness do not change much, a remarkable enhancement in plasticity occurs in the Zr<sub>58.6</sub>Cu<sub>18</sub>Ni<sub>10.4</sub>Al<sub>8</sub>Fe<sub>5</sub> BMG, which is presumably due to the restriction of the nano-scale second phase on shear banding. Phase separation was also found to promote multiple shear bands, enhanced toughness and oxidative wear, which work synergistically during the tribological test to improve the wear resistance of Zr–Cu–Ni–Al BMGs. These findings provide some insights into the wear mechanisms of dual-phase BMGs, which may offer new strategies for design and optimization of BMGs with desired wear performance.</p>
engineering, mechanical,materials science, multidisciplinary