Abstract:During the last two decades, the use of fiber-reinforced polymer (FRP) in the retrofitting of concrete structures has been widely studied. However, there is limited research on the effect of initial concrete damage on the retrofitting effect of FRP on concrete columns, especially when the initial damage is severe. For FRP-confined concrete columns, the fracture process inside the concrete is covered by FRP and is not visible to inspectors during the service period. This paper investigates these problems through an experimental study of 28 100 x 100 x 300 mm concrete columns using axial compression tests and acoustic emission (AE) fracture monitoring. Prior to FRP wrapping, three different damage levels were assigned to the concrete columns. The stress-strain results showed that the predamage levels had a small effect on the ultimate strength of the FRP-confined predamaged concrete columns, even when the predamage was severe, whereas the axial/lateral strains were more affected by the predamage levels. AE parameter analysis showed that at the early loading stage, AE signals generated from FRP-confined predamaged concrete columns contained less energy than those from the FRP-confined intact concrete columns. The fracture processes of unconfined and FRP-confined concrete columns were also studied through concrete failure modes, b-value and improved b-value (Ib-value) analyses, and fractal analysis. The following conclusions were drawn from the analyses: (1) during compression of the FRP-confined concrete columns, the concrete failure modes shifted from cracking type to cracking-crushing mixed type; (2) the fracture process of the confined concrete columns could be divided into three stages, which are different from those for unconfined concrete columns and reinforced concrete beams; (3) the fractal dimension of the crack network had a relationship with the b-value and decreased from a value between 3 and 2 to a final value of 2 during the fracture process for unconfined and FRP-confined concrete columns. DOI: 10.1061/(ASCE)CC.1943-5614.0000309. (C) 2012 American Society of Civil Engineers.

Damage Evaluation of Fiber Reinforced Plastic-Confined Circular Concrete-Filled Steel Tubular Columns under Cyclic Loading Using the Acoustic Emission Technique

Research on CFRP confined circular concrete-filled steel tubular columns subjected to cyclic lateral forces

Axial Impact Behavior of Confined Concrete Filled Square Steel Tubes Using Fiber Reinforced Polymer

Low-Cycle Fatigue Test of Circular Concrete Filled Tubular Columns

Low-Cycle Fatigue Damage of Circular Concrete-Filled-Tube Columns

Low Cyclic Fatigue Performance of Concrete-Filled Steel Tube Columns

Flexural behavior of concrete-filled circular steel tubes under high-strain rate impact loading

Impact Behaviors of CFT and CFRP Confined CFT Stub Columns

Damage evaluation and failure mechanism analysis of steel tube confined reinforced-concrete columns by acoustic emission technology

Seismic behavior and damage evaluation of self-sensing concrete-filled frp / frp-steel composite tubular columns for bridge

Cracking Mechanism of Corroded Reinforced Concrete Column Based on Acoustic Emission Technique

Acoustic emission monitoring and damage assessment of FRP-strengthened reinforced concrete columns under cyclic loading

Damage analysis of axially compressed concrete-filled steel tube stub columns based on acoustic emission

Acoustic Emission Study on the Damage Evolution of a Corroded Reinforced Concrete Column under Axial Loads

Acoustic Emission Monitoring of Concrete Columns and Beams Strengthened with Fiber Reinforced Polymer Sheets

Damage in carbon fiber-reinforced concrete, monitored by both electrical resistance measurement and acoustic emission analysis

Fatigue Damage Evolution and Monitoring of Carbon Fiber Reinforced Polymer Bridge Cable by Acoustic Emission Technique

Repair Effects and Acoustic Emission Technique–Based Fracture Evaluation for Predamaged Concrete Columns Confined with Fiber-Reinforced Polymers

Local Damage Identification of High-Strength Circular Concrete-Filled Steel Tubes under Low Cycle Fatigue

Acoustic Emission Assessment of Corroded RC Columns Jointly Reinforced with Concrete Canvas and CFRP

Damage analysis of concrete-filled square stainless steel columns based on acoustic emission and Markov chain methods