Abstract:The ability to undercool and solidification mechanism of liquid quinary Ni40Zr28.5Ti16.5Al10Cu5 alloy are investigated by electromagnetic levitation (EML) and drop tube (DT) technique. Under the EML condition, the maximum undercooling of levitated alloy can reach up to 290 K (0.21TL). Under the DT condition, the alloy achieves higher undercooling than EML, and solidifies finally into metallic glass. At lower undercooling, the solidification structure of the alloy is composed of primary Ni3Ti phase, secondary Ni10Zr7 phase and eutectic (Ni10Zr7+Ni21Zr8) phase. With the rise of undercooling, the solidification structure displays the following evolution events: phase morphology refinement, primary phase inhibition, phase number reduction, and amorphous phase formation. By using the high-speed cinematography technique, three nucleation modes are distinctly observed on the levitated alloy melt surface at the beginning of solidification, that is, single-point nucleation, multi-point nucleation and annular nucleation. The levitation state corresponding to single-point mode nucleation is relatively stable, and the alloy undercooling is also relatively low. The annular nucleation only occursin the case with high rotation speed, and the undercooling is greater than 208 K. The discrepancy between nucleation modes is due to the He gas flow for forced cooling. The theoretical calculations indicate that the alloy droplets achieve high undercoolingand large cooling rate under the DT condition. The experimental results show that when the droplet diameter decreases to 498 μm, the amorphous phase begins to appear in the alloy particles. It is noteworthy that the amorphous phase is preferentially formed inside the droplet, but not on the outer surface. The morphology of solidification structure reveals that different regions of the droplet have various local undercoolings, which result in the distribution characteristics of amorphous phase. The volume fraction of amorphous phase increases linearly with the decrease of particle diameter. When the droplet diameter decreases to 275 μm, the alloy droplets are completely frozen into glassy particles. The average eutecticspacing values are also measured at different alloy undercoolings. Compared with the classical binary eutectic growth model, the experimental eutectic growth law exhibits a large deviation in index. This indicates that the eutectic growth in multicomponent alloys displays more complex kinetic characteristics.

Numerical Study on the Impact of Cooling Rate on the Solidification of Al-Bi Hypermonotectic Alloys

Influence of Cooling Rate on the Formation of Bimodal Microstructures in Nickel-Base Superalloys During Continuous Two-Step Aging

Influences of Solution Cooling Rate on Microstructural Evolution of a Multiphase Ni3Al-based Intermetallic Alloy

Rapid Monotectic Solidification under Free Fall Condition

Rapid Solidification Mechanism of Liquid Quinary Ni-Zr-Ti-Al- Cu Alloy Investigated by High-Speed Cinematography

Combined Effects of High Undercooling and Large Cooling Rate on the Microstructure Evolution and Hardening Mechanism of Rapidly Solidified Ti-Al Alloys

Influence of Heating and Cooling Rate on Dissolution and Precipitation Behavior of Nickel-based Single Crystal Superalloy

Influences Of The Heating And Cooling Rates On The Dissolution And Precipitation Behavior Of A Nickel-Based Single-Crystal Superalloy

Influence of Cooling Scenarios on the Evolution of Microstructures in Nickel-Based Single Crystal Superalloys

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy

Metastable Phase Separation And Rapid Solidification Of Undercooled Co40fe40cu20 Alloy

Numerical Simulation of Recalescence of 3-Dimensional Isothermal Solidification for Binary Alloy Using Phase-Field Approach

The Effect of Cooling Rate on the Microstructure Change During Rapid Solidification of Liquid Ti3Al Alloy

Solidification Structure Evolution of Immiscible Al–Bi–Sn Alloys at Different Cooling Rates

Effects of Cooling Rate on the Solidification Process of Pure Metal Al: Molecular Dynamics Simulations Based on the MFPT Method

Coarsening Mode and Microstructure Evolution of Al–In Hypermonotectic Alloy During Rapidly Cooling Process

Effect of cooling rate on microstructure and mechanical properties of rapidly solidified Al-based bulk alloys

Numerical simulation on solute partition and solid fraction evolution in solidification of Al-Cu-Mg alloys

Microstructure Evolution of Immiscible Alloys During Rapid Cooling Through Miscibility Gap

Solidification Behavior of Ni-based Superalloy at Different Cooling Rates

Structural Origin Underlying the Effect of Cooling Rate on Solidification Point