Effects of Eu3+-doped Concentration and Matricial Oxygen Vacancies on the Luminescence Properties of Ca2-xEuxSnO4

WANG Xiao-fang,ZHANG Chi,DENG Chao-yong

DOI: https://doi.org/10.3788/fgxb20163709.1037

2016-01-01

Abstract:Ca2-xSnO4∶xEu3+(x=0, 0. 001, 0. 005, 0. 01, 0. 015, 0. 02)phosphors were prepared by solid-state reaction method in air and vacuum atmosphere, respectively. The influence of Eu3+-doped concentration and oxygen vacancies on the luminescence properties were investigated. With the increas-ing of Eu3+ concentration, the emission intensity increases and the two main emission peaks at 614 nm and 618 nm gradually become one at about 616 nm. In the excitation spectra of Ca2-x SnO4∶xEu3+, the band between 200 nm and 295 nm is charge transfer band of Eu3+-O2-. The peak of charge transfer band moves from 271 nm to 286 nm with increasing Eu3+ concentration. In addition, under the same concen-tration of Eu3+, the luminescence intensity of samples sintered in vacuum is twice as much as that in air. Because the oxygen vacancies increase in the samples sintered in vacuum atmosphere, the conduction electron density rises, which leads to the higher emission intensity. Furthermore, the increase of electron trap leads to the improvement of afterglow properties of Ca2-x SnO4∶xEu3+.