Abstract:Eu single doped and Eu, B co-doped SiO2 xerogels and films were prepared by sol-gel process, using tetraethoxy silane, boric acid and aluminium nitrate as precursors, europium nitrate as the dopant. The influence of B ions and annealing temperature on luminescent properties of phosphors has been studied using fluorescence spectrum, X-ray diffraction and IR spectrum. The phosphors showed prominent luminescent in red. When heated up to 500°C, the emission spectrum showed six characteristic emission peaks, due to the electronic transition of5D0→7FJ (J = 0, 1, 2, 3, 4) for Eu3+ respectively and the electronic transition of 5D0→7F1 was splited two peaks. When B ions were introduced to the Eu doped samples, the red Eu3+ emission was enhanced remarkably. This is because Si-O-B bonds were formed in the luminescent materials, and the symmetry of network was breached. Annealing changed the network structure and reduced the content of -OH and water, which benefits intensity of emission from Eu3+. The intensity of emission from Eu3+ quenches with increasing of annealing (up to 850°C) for probability during the annealing process, the rare earth ions may migrate and form clusters. The clustering process makes the local concentration of Eu very high and causes serious fluorescence quenching. XRD results show that the phosphor is in amorphous phase.

The Luminescence Enhancement Of Eu3+ Ion And Sno2 Nanocrystal Co-Doped Sol-Gel Sio2 Films

The Luminescence Enhancement of Eu 3+ Ion and SnO 2 Nanocrystal Co-Doped Sol Gel SiO 2 Films

Preparation and Photoluminescence Properties of Eu3+-Doped Al2O3 Films on Silicon Substrates by the Sol-gel Method

Energy Transfer Process Between Eu3+ and Wide-Band-gap SnO2 Nanocrystals in Silica Films Studied by Photoluminescence Excitation and Time-Resolved Photoluminescence Techniques

Luminescence Enhancement Due to Energy Transfer in ZnO Nanoparticles and Eu3+ Ions Co-Doped Silica

Luminescence Behavior of Eu(Ttfa)(3) Doped B2o3-Sio2 Film Prepared by Sol-Gel Process

Influences of Doping and Annealing Conditions on the Photoluminescence from In2O3 Nanocrystals and Eu3+ Ions Co-Doped Sol-Gel SiO2 Films

Preparation and Luminescence of Nano-Sized In2O3and Rare-Earth Co-Doped SiO2thin Films

Photoluminescence from Er3+ Ion and SnO2 Nanocrystal Co-Doped Silica Thin Films

Study of Eu3+-doped Luminescence Glasses Prepared by a Sol-Gel Process

Energy Transfer and Enhanced Luminescence in Metal Oxide Nanoparticle and Rare Earth Codoped Silica

Structure and Luminescence Evolution of Annealed Europium-doped Silicon Oxides Films

Luminescence properties of Eu2+ and Mn2+ Codoped 50SiO2-17Al2O3-23MgF2-10NaF glasses and glass-ceramics

Fabrication and luminescence properties Eu3+ doped SiO2 thin films

Structure And Photoluminescence Property Of Eu-Doped Sno(2) Nanocrystalline Powders Fabricated By Sol-Gel Calcination Process

Growth of SnO2 nanocrystals co-doped with Eu3+ for highly enhanced photoluminescence in mesoporous silica glasses

Improved Sensitization Efficiency In Er3+ Ions And Sno2 Nanocrystals Co-Doped Silica Thin Films

Enhanced emission from Eu3+ in B ions doped sol-gel SiO2 phosphors

Improved Resonant Energy Transfer and Light Emission from SnO2 Nanocrystals and Er3+ Embedded in Silica Films Via Yb3+ Co-Doping

Structure And Luminescence Properties Of Eu3+ Doped Sio2 Glass Synthesized By Sol-Gel Process

A Facile Method for the Fabrication of Luminescent Eu3+-Doped SiO2 Nanowires