Abstract:In this study, a simple and low-cost method to synthesize iron(III) oxide nanopowders in large quantity was successfully developed for the photocatalytic degradation of microcystin-LR (MC-LR). Two visible light-active iron(III) oxide samples (MG-9 calcined at 200 °C for 5 h and MG-11 calcined at 180 °C for 16 h) with a particle size of 5–20 nm were prepared via thermal decomposition of ferrous oxalate dihydrate in air without any other modifications such as doping. The synthesized samples were characterized by X-ray powder diffraction, 57Fe Mössbauer spectroscopy, transmission electron microscopy, Brunauer–Emmett–Teller (BET) specific surface area analysis, and UV–visible diffuse reflectance spectroscopy. The samples exhibited similar phase composition (a mixture of α-Fe2O3 and γ-Fe2O3), particle size distribution (5–20 nm), particle morphology, and degree of agglomeration, but different specific surface areas (234 m2 g−1 for MG-9 and 207 m2 g−1 for MG-11). The results confirmed higher photocatalytic activity of the catalyst with higher specific surface area. The highest photocatalytic activity of the sample to decompose MC-LR was observed at solution pH of 3.0 and catalyst loading of 0.5 g L−1 due to large amount of MC-LR adsorption, but a little iron dissolution of 0.0065 wt% was observed. However, no iron leaching was observed at pH 5.8 even though the overall MC-LR removal was slightly lower than at pH 3.0. Thus, the pH 5.8 could be an appropriate operating condition for the catalyst to avoid problems of iron contamination by the catalyst. Moreover, magnetic behavior of γ-Fe2O3 gives a possibility for an easy separation of the catalyst particles after their use.

Microcystin-Lr Degradation by Hydrogen-Terminated Porous Si under Visible Light Irradiation

Experimental and Model Comparisons of H2O2 Assisted UV Photodegradation of Microcystin-LR in Simulated Drinking Water

Degradation of Ciprofloxacin by TiO2/Fe2O3/zeolite Catalyst-Activated Persulfate under Visible LED Light Irradiation

[Degradation of MC-LR by Combination of UV/H2O2 Process].

Photodegradation of Microcystin-Lr Catalyzed by Metal Phthalocyanines Immobilized on Tio2-Sio2 under Visible-Light Irradiation

Study on Kinetics of Microcystin-LR Degradation by Ozonation

A Novel Photocatalytic Material for Removing Microcystin-Lr under Visible Light Irradiation: Degradation Characteristics and Mechanisms.

Inactivation of Microcystis Aeruginosa by Hydrogen-Terminated Porous Si Wafer: Performance and Mechanisms.

Process Optimization for Microcystin-Lr Degradation by Response Surface Methodology and Mechanism Analysis in Gas-Liquid Hybrid Discharge System

Degradation of microcystin-LR with expanded graphite based photocatalysts: Performance and mechanism based on active sites-radicals interaction

Oxidation and Biotoxicity Assessment of Microcystin-Lr Using Different AOPs Based on UV, O-3 and H2O2

Photodegradation of MC-LR using a novel Au-decorated Ni metal-organic framework (Au/Ni-MOF)

The Optical Properties of Porous Silicon Produced by Metal-Assisted Anodic Etching

Degradation of Microcystin-Lr by Highly Efficient AgBr/Ag3PO4/TiO2 Heterojunction Photocatalyst under Simulated Solar Light Irradiation

Developing self-floating N-defective graphitic carbon nitride photocatalyst for efficient photodegradation of Microcystin-LR under visible light

Photocatalytic degradation of microcystin-LR with a nanostructured photocatalyst based on upconversion nanoparticles@TiO 2 composite under simulated solar lights

Oxidative degradation of microcystin-LR by combination of UV/H2O2.

Degradation of the cyanotoxin microcystin-LR using iron-based photocatalysts under visible light illumination

Using a Novel Hydrogen-Terminated Porous Si Wafer to Enhance Microcystis Aeruginosa Effective Removal by Chitosan at a Low Dosage

[Mechanism of Photochemical Degradation of MC-LR by Pyrite]

An Alternative to in Situ Photocatalytic Degradation of Microcystin-Lr by Worm-Like N, P Co-Doped Tio2/Expanded Graphite by Carbon Layer (Npt-Egc) Floating Composites