Preparation of Bipolar Membranes by Electrospinning

Jiefeng Pan,Linxiao Hou,Qiuyue Wang,Yubin He,Liang Wu,Abhishek N. Mondal,Tongwen Xu

DOI: https://doi.org/10.1016/j.matchemphys.2016.11.023

IF: 4.778

2016-01-01

Materials Chemistry and Physics

Abstract:A new preparative pathway for the bipolar membranes was initiated via the electrospinning and hot-press process. The prepared bipolar membrane was consisting of sulfonated poly (phenylene oxide), polyethylene glycol, and quaternized poly (phenylene oxide). The above mentioned membrane was fabricated by the continuous electrospinning of the respective layer, followed by the solvent atmosphere treatment and hot-pressing, to obtain a transparent and dense structure. The thickness of each layer can be easily tuned by controlling the electrospinning parameters. The clear interfacial structure was observed and confirmed by the scanning electron microscope. The bipolar performance is evaluated by the current–voltage curves and production yield of acid and base. The final optimized bipolar membrane had similar yield of acid and base as the casting membrane. However, extremely lower potential drop value was observed when they are applied for the production of acid and base. The experimental results showed that, electrospinning is an effective and well controlled way to fabricate bipolar membranes, in which anion or cation exchange layer as well as interfacial layer can be easily changed or added as requested.