Abstract:Thermoplastic vulcanizates (TPV) is a class of thermoplastic elastomer of which generally consists of polyolefin phase, mainly PP or PE, with dynamically cured elastomer phase such as EPDM. The elastomer should be well dispersed in the polyolefin matrix which facilitates thermoplastic like processing of elastomer. The properties of TPV are mainly governed by properties of thermoplastic matrix and vulcanized rubber phases including curing system used for dynamic vulcanization. As environmental problem has been an important issue, application of bioplastic in thermoplastic elastomer is an interesting issue. The blending of NR with various has been studied in our work and the system should classify as bioplastics/NR. Dynamic vulcanization of NR during melt blending of NR with various bioplastics was also studied. In this report, the melt blending system of PBAT/NR; PCL/NR and PBS/NR were carried out. The batch melt blending in an internal mixer were performed with various NR and bioplastics compositions. Dynamic vulcanization of NR phase, using Luperox® 101 as curing agent, was also occurred in the mixer during melt blending. Except for PBS/NR TPV system where dicumyl peroxide was used as curing agent. This will advantage for foam preparation in further foaming step. The results showed that PBAT/NR TPV with NR content as high as 70% possessed tension set less than 20% and elongation at break under tension was higher than 600%. For PCL/NR system at the same composition, the tension set was also found at 20%, elongation at break under tension was as high as 1000%. The TPV system of PBAT/NR and PCL/NR were also extrudable. Tension set for NR/PBS TPV system was found at about 30% and the elongation at break under tension was about 600%. From the mentioned basic properties of biobased TPV in our researches, it presents that they could propose the promising qualified TPV, in term of reprocess ability and advantage for the sake of biodegradability. Note: PBAT, PCL and PBS stand for poly(butylene adipate-co-terepthalate, polycarprolactone, and poly(butylene succinate) respectively.

Super-tough Poly(lactide) Thermoplastic Vulcanizates Based on Modified Natural Rubber

A super-toughened poly(lactic acid)-based thermoplastic vulcanizate through incorporating modified SiO2 nanoparticles

A super-toughened poly(lactic acid)-based thermoplastic vulcanizate through incorporating modified SiO<sub>2</sub> nanoparticles

Super-Tough Poly(lactic Acid)-Based Thermoplastic Vulcanizate Based on Selective Dispersion and in Situ Compatibilization of Commercial Reinforcing Fillers and Its Application in Three-Dimensional Printing

Fully biobased and supertough polylactide-based thermoplastic vulcanizates fabricated by peroxide-induced dynamic vulcanization and interfacial compatibilization

Super-tough poly(lactic acid)/silicone rubber thermoplastic vulcanizates: The organic and inorganic synergistic interfacial compatibilization

A New Strategy for the Preparation of Fully Biobased and Biodegradable Polylactic Acid with Both High Rigidity and Flexibility

Novel Biobased Thermoplastic Elastomer Consisting of Synthetic Polyester Elastomer and Polylactide by in Situ Dynamical Crosslinking Method

Largely toughened poly(lactic acid) fabricated by melt blending with thermoplastic polyurethane through interfacial compatibilization induced by simultaneous addition of hydrophobic silica nanoparticles and in situ cross‐linking reaction

Super-tough Polylactic Acid Blends Via Tunable Dynamic Vulcanization of Biobased Polyurethanes

Highly Toughened and Heat-Resistant Poly(lactic acid) with Balanced Strength Using an Unsaturated Liquid Crystalline Polyester via Dynamic Vulcanization

Bio-based thermoplastic vulcanizates from natural rubber (bioplastic/NR)

Dynamically vulcanized polylactic acid/natural rubber/waste rubber blends: effect of the rubber content

Crosslinked bicontinuous biobased polylactide/natural rubber materials: Super toughness, “net-like”-structure of NR phase and excellent interfacial adhesion

PLA/PCL/NR ternary blown films with high ductility and thermal shrinkage performance via dynamic vulcanization

Supertough poly(lactic acid)/bio-polyurethane blends fabricated by dynamic self-vulcanization of dual difunctional monomers

Supertough Shape Memory Bionanocomposites of Thermoplastic Vulcanizates Based on PLA- EVA and Cellulose Nanocrystal

Biobased Foamed Thermoplastic Vulcanizate with Good Electromagnetic Interference and Self-Healing Performance

Shape memory polylactic acid/modified Eucommia ulmoides gum thermoplastic vulcanizates based on excellent interfacial adhesion and co‐continuous structure

Selectively Cross-Linked Poly (Lactide)/ethylene-Glycidyl Methacrylate-Vinyl Acetate Thermoplastic Elastomers with Partial Dual-Continuous Network-Like Structures and Shape Memory Performances

Biobased Poly(lactide)/ethylene-co-vinyl Acetate Thermoplastic Vulcanizates: Morphology Evolution, Superior Properties, and Partial Degradability