Abstract:Zn–Ni, Zn–Co and Zn–Ni–Co coatings were electrodeposited on mild steel from an acidic chloride bath containing p-aminobenzenesulphonic acid (SA) and gelatin. These additives changed the phase content in the coatings, most likely as a result of their adsorption at the surface of the cathode. The effect of gelatin was more pronounced than that of SA. The Faradaic efficiency was higher than 90%. As the current density was increased or the bath temperature was decreased, the concentration of the nobler metal in the coating increased. Both concentrations of Ni and Co in the ternary alloy increased as the applied current density was increased. Nickel and cobalt were found to have a synergistic catalytic effect. The thickness of all coatings increased as the applied current density was increased. The hardness increased with current density to a peak value, and then decreased. The rate of Zn deposition was heavily influenced by mass-transport limitation at high applied current densities, while the rates of Ni and Co deposition were not. The anomalous codeposition was explained by the great difference between the exchange current densities of Zn and the iron-group metal. Potentiodynamic polarization scans and electrochemical impedance spectroscopy showed that the corrosion resistance of the ternary Zn–Ni–Co alloy coatings was approximately 10 times higher than that of Zn–Ni and 7 times higher than that of Zn–Co. The improved corrosion resistance of the ternary alloy was attributed to its surface chemistry, phase content, texture, and surface morphology. The ternary Zn–Ni–Co coating may thus replace the conventional Zn–Ni and Zn–Co coatings in a variety of applications.

The Electrodeposition of Zn-Co Alloy from a Zincate Bath

Direct copper electrodeposition onto cobalt adhesion layer in alkaline bath

ZINC-NICKEL ALLOY ELECTROPLATING IN AN ALKALINE BATH

Electrodeposition and corrosion performance of Ni-Co alloys with different cobalt contents

The Performance of Zn-Ni Alloy Coating Electrodeposited from Stabilized Bath

Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys

Electrodeposition, Morphology, Composition, and Corrosion Performance of Zn-Mn Coatings from a Deep Eutectic Solvent

Electrodeposition of Ni–Co alloys from a deep eutectic solvent

Potassium salt based alkaline bath for deposition of Zn–Fe alloys

Effect of citrate additive on the electrodeposition and corrosion behaviour of Zn–Co alloy

Comparative study of zinc base alloy coatings: composition, microstructure, and corrosion resistance

Electroplating and Physicochemical Properties of Zinc–Nickel Alloy Coatings from Ammonium Oxalate Electrolytes

Electrochemical synthesis of SnCo alloy shells on orderly rod-shaped Cu current collectors as anode materials for lithium-ion batteries with enhanced performance

Electrodeposition and characterization of Zn–Sn alloy coatings from a deep eutectic solvent based on choline chloride for corrosion protection

Eco-Friendly Electrodeposition of Al-Zn Alloy from AlCl3-Urea Deep Eutectic Solvent

Electrodeposition of decorative and protective Zn–Fe coating onto low-carbon steel substrate

Rapid Electrodeposition and Corrosion Behavior of Zn Coating from a Designed Deep Eutectic Solvent

Electrodeposition of Nanostructured Co–Cu Thin Alloy Films on to Steel Substrate from an Environmentally Friendly Novel Lactate Bath under Different Operating Conditions

Preparation and Properties of Al/Pb-Ag-Co Composite Anode Material for Zinc Electrowinning

Effect of Electroplating Bath Composition on Corrosion Resistance of Deposited Cobalt Films

Electrodeposition of High Entropy Alloy of Ni-Co-Cu-Mo-W from an Aqueous Bath